As2 Au K5 Eisenmann B, Klein J, Somer M Journal of Alloys and Compounds 178 (1992) 431-439 Linear anions (CuAs2)5-, (AuP/2)5- and (AuAs2)5- in potassium compounds _cod_database_code 1008878 _database_code_amcsd 0016745 CELL PARAMETERS: 5.7300 5.7300 19.2160 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 546.390 Density (g/cm3): 3.296 MAX. ABS. INTENSITY / VOLUME**2: 72.14113054 RIR: 7.127 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.20 62.76 9.6080 0 0 2 2 17.87 31.25 4.9623 1 0 0 6 18.47 100.00 4.8047 1 0 1 12 20.14 6.51 4.4090 1 0 2 12 22.67 11.98 3.9228 1 0 3 12 25.81 16.34 3.4516 1 0 4 12 27.86 6.98 3.2027 0 0 6 2 31.22 99.95 2.8650 1 1 0 6 32.61 20.41 2.7455 1 1 2 12 33.30 21.62 2.6909 1 0 6 12 36.20 5.28 2.4812 2 0 0 6 36.51 18.37 2.4607 2 0 1 12 37.43 1.49 2.4024 2 0 2 12 37.44 34.87 2.4021 1 0 7 12 37.44 8.45 2.4020 0 0 8 2 38.93 2.86 2.3136 2 0 3 12 40.94 4.06 2.2045 2 0 4 12 41.78 4.90 2.1620 1 0 8 12 42.33 13.03 2.1353 1 1 6 12 46.29 7.65 1.9614 2 0 6 12 46.29 8.00 1.9613 1 0 9 12 47.30 3.95 1.9216 0 0 10 2 48.54 4.47 1.8756 2 1 0 12 48.78 16.02 1.8667 2 1 1 24 49.52 1.38 1.8408 2 1 2 24 49.52 14.80 1.8407 2 0 7 12 49.52 21.68 1.8407 1 1 8 12 50.72 2.45 1.8000 2 1 3 24 52.37 3.33 1.7471 2 1 4 24 53.07 2.44 1.7258 2 0 8 12 55.56 16.01 1.6541 3 0 0 6 56.45 3.91 1.6301 3 0 2 12 56.89 7.43 1.6185 2 1 6 24 56.89 4.28 1.6184 2 0 9 12 57.77 11.58 1.5959 1 1 10 12 59.71 15.97 1.5486 2 1 7 24 62.86 2.89 1.4783 2 1 8 24 63.28 3.56 1.4697 3 0 6 12 65.12 9.13 1.4325 2 2 0 6 65.93 2.33 1.4168 2 2 2 12 66.34 5.26 1.4091 2 1 9 24 68.13 1.51 1.3763 3 1 0 12 68.33 5.58 1.3728 3 1 1 24 68.93 7.29 1.3623 3 0 8 12 71.28 1.01 1.3231 3 1 4 24 71.29 2.09 1.3229 1 0 14 12 72.25 2.29 1.3077 2 2 6 12 75.13 2.75 1.2645 3 1 6 24 75.90 4.31 1.2536 3 0 10 12 76.85 1.73 1.2404 1 0 15 12 77.03 1.93 1.2380 4 0 1 12 77.04 2.11 1.2378 1 1 14 12 77.60 6.73 1.2303 3 1 7 24 77.60 4.99 1.2303 2 2 8 12 79.86 1.43 1.2010 2 0 14 12 80.42 1.37 1.1942 3 1 8 24 82.67 1.80 1.1673 1 0 16 12 83.58 2.64 1.1568 3 1 9 24 84.33 3.08 1.1485 2 2 10 12 85.26 1.31 1.1383 2 0 15 12 85.99 2.51 1.1305 4 0 7 12 88.21 2.14 1.1077 2 1 14 24 88.22 3.44 1.1076 1 1 16 12 88.77 1.64 1.1021 1 0 17 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.