Fe17 Th2 Isnard O, Soubeyroux J, Fruchart D, Jacobs T, Buschow K Journal of Alloys and Compounds 186 (1992) 135-145 Structural and magnetic behaviour of the series Th2Fe17Cx (x=0 to 1.25) _cod_database_code 1008582 _database_code_amcsd 0016473 CELL PARAMETERS: 8.6990 8.6990 12.5330 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 821.343 Density (g/cm3): 8.650 MAX. ABS. INTENSITY / VOLUME**2: 135.2098219 RIR: 5.090 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.71 5.20 6.4568 1 0 1 6 18.42 5.35 4.8177 0 1 2 6 20.42 20.97 4.3495 1 1 0 6 21.27 8.55 4.1777 0 0 3 2 24.68 12.63 3.6074 0 2 1 6 27.63 7.57 3.2284 2 0 2 6 29.65 66.97 3.0130 1 1 3 12 30.91 14.32 2.8930 1 0 4 6 32.24 15.69 2.7767 2 1 1 12 34.60 10.82 2.5923 1 2 2 12 35.76 46.02 2.5112 3 0 0 6 37.33 29.78 2.4088 0 2 4 6 37.83 1.62 2.3784 0 1 5 6 41.52 68.99 2.1748 2 2 0 6 41.98 49.40 2.1523 0 3 3 6 41.98 50.60 2.1523 3 0 3 6 42.92 22.00 2.1072 2 1 4 12 43.32 30.58 2.0888 0 0 6 2 43.36 12.82 2.0868 2 0 5 6 47.11 6.14 1.9290 2 2 3 12 48.38 7.47 1.8815 1 2 5 12 48.90 1.28 1.8625 4 0 1 6 50.61 1.47 1.8037 0 4 2 6 52.54 4.42 1.7419 1 0 7 6 52.65 3.79 1.7384 1 3 4 12 53.52 4.55 1.7121 3 2 1 12 55.12 6.34 1.6661 2 3 2 12 55.93 6.15 1.6440 4 1 0 12 56.95 3.29 1.6171 0 2 7 6 57.38 4.33 1.6059 0 3 6 6 57.38 3.94 1.6059 3 0 6 6 60.52 12.21 1.5298 1 4 3 12 60.52 11.77 1.5298 4 1 3 12 61.14 10.36 1.5157 2 1 7 12 61.25 10.82 1.5134 3 2 4 12 61.56 19.01 1.5065 2 2 6 12 62.04 1.41 1.4959 0 5 1 6 64.24 3.97 1.4498 3 3 0 6 65.61 3.15 1.4229 2 3 5 12 66.05 1.00 1.4146 2 4 1 12 68.50 12.48 1.3697 3 3 3 12 69.09 2.46 1.3596 1 3 7 12 69.19 2.23 1.3579 0 5 4 6 69.93 2.71 1.3452 5 1 1 12 71.08 5.41 1.3262 1 1 9 12 71.31 2.26 1.3226 1 5 2 12 72.99 5.63 1.2962 2 4 4 12 73.31 1.17 1.2914 5 0 5 6 75.76 12.34 1.2556 6 0 0 6 76.63 5.73 1.2435 3 2 7 12 76.72 4.77 1.2422 5 1 4 12 77.03 3.05 1.2380 4 2 5 12 78.55 6.45 1.2178 0 3 9 6 78.55 6.86 1.2178 3 0 9 6 79.60 1.41 1.2044 0 4 8 6 80.67 1.04 1.1910 3 3 6 12 80.70 2.29 1.1907 1 5 5 12 80.82 1.96 1.1892 0 2 10 6 83.24 1.15 1.1607 2 3 8 12 83.39 1.19 1.1590 5 2 3 12 83.39 1.10 1.1590 2 5 3 12 83.94 2.02 1.1528 0 5 7 6 84.45 1.01 1.1471 2 1 10 12 87.55 1.34 1.1143 2 4 7 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.