Ce2 Fe17 N3 Isnard O, Miraglia S, Soubeyroux J, Fruchart D Journal of Alloys and Compounds 190 (1992) 129-135 Nitrogen gas pressure synthesis and neutron diffraction study of R2Fe17N3 with R=Ce and Nd _cod_database_code 1008558 _database_code_amcsd 0016449 CELL PARAMETERS: 8.7370 8.7370 12.7020 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 839.706 Density (g/cm3): 7.543 MAX. ABS. INTENSITY / VOLUME**2: 78.15243942 RIR: 3.374 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.24 1.37 4.8645 0 1 2 6 20.33 1.17 4.3685 1 1 0 6 20.98 3.34 4.2340 0 0 3 2 24.55 3.71 3.6258 0 2 1 6 27.44 1.98 3.2503 2 0 2 6 29.38 38.70 3.0403 1 1 3 12 30.53 11.09 2.9281 1 0 4 6 32.08 14.47 2.7900 2 1 1 12 34.39 8.37 2.6077 1 2 2 12 35.60 37.52 2.5222 3 0 0 6 36.96 31.54 2.4323 0 2 4 6 41.34 84.62 2.1843 2 2 0 6 41.68 48.34 2.1668 0 3 3 6 41.68 51.66 2.1668 3 0 3 6 42.54 21.41 2.1251 2 1 4 12 42.71 40.31 2.1170 0 0 6 2 42.88 16.28 2.1090 2 0 5 6 43.72 1.15 2.0705 1 3 1 12 46.80 24.88 1.9412 2 2 3 12 47.74 5.44 1.9051 1 1 6 12 47.90 9.41 1.8993 1 2 5 12 48.67 6.89 1.8710 4 0 1 6 50.33 6.85 1.8129 0 4 2 6 51.81 3.50 1.7645 1 0 7 6 52.25 2.16 1.7508 1 3 4 12 53.26 2.89 1.7199 3 2 1 12 54.83 8.20 1.6744 2 3 2 12 55.67 2.63 1.6511 4 1 0 12 56.22 1.73 1.6361 0 2 7 6 56.78 2.31 1.6215 0 3 6 6 56.78 1.56 1.6215 3 0 6 6 60.15 9.85 1.5383 1 4 3 12 60.15 8.78 1.5383 4 1 3 12 60.42 11.43 1.5322 2 1 7 12 60.81 12.63 1.5231 3 2 4 12 60.95 19.07 1.5202 2 2 6 12 61.73 1.26 1.5027 0 5 1 6 63.93 2.12 1.4562 3 3 0 6 65.08 2.81 1.4332 2 3 5 12 68.09 9.39 1.3770 3 3 3 12 68.34 1.51 1.3726 1 3 7 12 68.71 1.60 1.3661 0 5 4 6 69.57 2.70 1.3513 5 1 1 12 70.06 3.42 1.3430 1 1 9 12 70.92 2.18 1.3289 1 5 2 12 72.49 5.62 1.3038 2 4 4 12 72.74 1.46 1.3001 5 0 5 6 75.37 14.07 1.2611 6 0 0 6 75.85 5.92 1.2543 3 2 7 12 76.20 5.01 1.2494 5 1 4 12 76.44 3.87 1.2461 4 2 5 12 77.50 7.34 1.2316 3 0 9 6 77.50 6.19 1.2316 0 3 9 6 78.68 4.05 1.2161 0 4 8 6 79.62 1.66 1.2041 0 2 10 6 80.08 2.97 1.1983 1 5 5 12 81.13 1.30 1.1854 2 2 9 12 82.30 1.92 1.1716 2 3 8 12 83.11 2.08 1.1622 0 5 7 6 84.96 1.08 1.1415 0 1 11 6 89.80 3.80 1.0921 4 4 0 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.