Os3.32 Si0.68 U2
      Verniere A, Lejay P, Bordet P, Chenavas J, Brison J, Haen P, Boucherle J
      Journal of Alloys and Compounds 209 (1994) 251-255
      Crystal structures and physical properties of some new ternary
      compounds U2 T3X (T= Ru, Os; X= Si, Ge)
      _cod_database_code 1008673
      _database_code_amcsd 0016559

      CELL PARAMETERS:    7.4360   7.4360   7.4360   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    411.167
      Density (g/cm3):     18.199
      MAX. ABS. INTENSITY / VOLUME**2:      1268.371631    
      RIR:     22.693
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                34.10         40.04        2.6290    2   2   0        12
                40.22        100.00        2.2420    3   1   1        24
                42.09         29.26        2.1466    2   2   2         8
                49.00          1.21        1.8590    4   0   0         6
                61.05         12.64        1.5179    4   2   2        24
                65.19         20.21        1.4311    5   1   1        24
                65.19          6.74        1.4311    3   3   3         8
                71.81         21.01        1.3145    4   4   0        12
                81.94          4.67        1.1757    6   2   0        24
                85.66          8.17        1.1340    5   3   3        24
                86.90          7.82        1.1210    6   2   2        24
================================================================================