Co0.2 Cr1.8 D3.615 Zr Soubeyroux J, Bououdina M, Fruchart D, Pontonnier L Journal of Alloys and Compounds 219 (1995) 48-54 Phase stability and neutron diffraction studies of Laves phases Zr (Cr1-x Mx)2 with M =Mn,Fe,Co,Ni,Cu and 0 < x <0.2 and their hydrides _cod_database_code 1008682 _database_code_amcsd 0016568 CELL PARAMETERS: 5.3700 5.3700 8.7890 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 219.492 Density (g/cm3): 6.059 MAX. ABS. INTENSITY / VOLUME**2: 81.05391629 RIR: 4.356 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.62 3.32 4.1106 1 0 1 12 27.93 7.13 3.1941 1 0 2 12 33.37 48.97 2.6850 1 1 0 6 36.24 88.21 2.4788 1 0 3 12 38.72 13.29 2.3253 2 0 0 6 39.32 100.00 2.2912 1 1 2 12 40.11 74.12 2.2479 2 0 1 12 41.08 11.19 2.1972 0 0 4 2 44.06 6.75 2.0553 2 0 2 12 45.67 10.58 1.9867 1 0 4 12 55.92 5.61 1.6443 1 0 5 12 59.64 8.06 1.5502 3 0 0 6 61.52 35.40 1.5073 2 1 3 24 63.51 4.10 1.4648 0 0 6 2 63.65 20.46 1.4619 3 0 2 12 66.70 24.62 1.4022 2 0 5 12 66.98 2.81 1.3972 1 0 6 12 68.34 3.44 1.3726 2 1 4 24 70.09 20.88 1.3425 2 2 0 6 76.67 3.15 1.2429 2 1 5 24 76.93 8.20 1.2394 2 0 6 12 78.99 1.15 1.2122 1 0 7 12 81.54 12.20 1.1805 3 1 3 24 83.07 1.07 1.1626 4 0 0 6 83.96 5.90 1.1526 4 0 1 12 84.59 5.30 1.1456 2 2 4 12 86.48 3.40 1.1253 2 1 6 24 87.75 2.17 1.1123 3 1 4 24 88.50 1.19 1.1048 2 0 7 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.