Cr1.8 D3.525 Ni0.2 Zr Soubeyroux J, Bououdina M, Fruchart D, Pontonnier L Journal of Alloys and Compounds 219 (1995) 48-54 Phase stability and neutron diffraction studies of Laves phases Zr (Cr1-x Mx)2 with M =Mn,Fe,Co,Ni,Cu and 0 < x <0.2 and their hydrides _cod_database_code 1008683 _database_code_amcsd 0016569 CELL PARAMETERS: 5.3670 5.3670 8.7930 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 219.347 Density (g/cm3): 6.059 MAX. ABS. INTENSITY / VOLUME**2: 84.40595272 RIR: 4.536 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 21.63 1.80 4.1092 1 0 1 12 27.93 5.94 3.1940 1 0 2 12 33.39 46.77 2.6835 1 1 0 6 36.23 85.30 2.4792 1 0 3 12 38.75 12.83 2.3240 2 0 0 6 39.34 100.00 2.2905 1 1 2 12 40.13 70.58 2.2468 2 0 1 12 41.06 12.03 2.1983 0 0 4 2 44.08 6.48 2.0546 2 0 2 12 45.65 8.29 1.9872 1 0 4 12 55.90 5.60 1.6448 1 0 5 12 56.40 1.40 1.6313 2 1 2 24 59.68 7.77 1.5493 3 0 0 6 61.54 31.74 1.5068 2 1 3 24 63.48 3.69 1.4655 0 0 6 2 63.68 20.31 1.4612 3 0 2 12 66.70 24.76 1.4023 2 0 5 12 66.95 2.71 1.3977 1 0 6 12 68.35 3.73 1.3724 2 1 4 24 70.14 20.35 1.3418 2 2 0 6 76.67 3.74 1.2429 2 1 5 24 76.91 7.58 1.2396 2 0 6 12 78.95 1.67 1.2126 1 0 7 12 81.58 11.95 1.1800 3 1 3 24 83.13 1.05 1.1620 4 0 0 6 84.01 5.70 1.1520 4 0 1 12 84.62 5.83 1.1453 2 2 4 12 86.48 2.50 1.1253 2 1 6 24 87.78 1.72 1.1120 3 1 4 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.