Cr1.8 D3.8 Mn0.2 Zr Soubeyroux J, Bououdina M, Fruchart D, Pontonnier L Journal of Alloys and Compounds 219 (1995) 48-54 Phase stability and neutron diffraction studies of Laves phases Zr (Cr1-x Mx)2 with M =Mn,Fe,Co,Ni,Cu and 0 < x <0.2 and their hydrides _cod_database_code 1008686 _database_code_amcsd 0016572 CELL PARAMETERS: 7.7540 7.7540 7.7540 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 466.206 Density (g/cm3): 5.688 MAX. ABS. INTENSITY / VOLUME**2: 159.8875959 RIR: 9.153 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.83 1.40 4.4768 1 1 1 8 32.66 46.45 2.7415 2 2 0 12 38.51 100.00 2.3379 3 1 1 24 40.29 24.06 2.2384 2 2 2 8 58.30 15.80 1.5828 4 2 2 24 62.21 20.49 1.4923 5 1 1 24 62.21 6.94 1.4923 3 3 3 8 68.45 20.30 1.3707 4 4 0 12 77.92 5.82 1.2260 6 2 0 24 81.38 8.10 1.1825 5 3 3 24 82.52 5.99 1.1690 6 2 2 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.