Cr1.8 D3.65 Fe0.2 Zr
      Soubeyroux J, Bououdina M, Fruchart D, Pontonnier L
      Journal of Alloys and Compounds 219 (1995) 48-54
      Phase stability and neutron diffraction studies of Laves phases Zr (Cr1-x Mx)2
      with M =Mn,Fe,Co,Ni,Cu and 0 < x <0.2 and their hydrides
      _cod_database_code 1008687
      _database_code_amcsd 0016573

      CELL PARAMETERS:    7.6551   7.6551   7.6551   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    448.593
      Density (g/cm3):      5.912
      MAX. ABS. INTENSITY / VOLUME**2:      166.7781376    
      RIR:      9.186
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                20.09          1.32        4.4197    1   1   1         8
                33.10         46.40        2.7065    2   2   0        12
                39.02        100.00        2.3081    3   1   1        24
                40.83         24.17        2.2098    2   2   2         8
                59.12         15.57        1.5626    4   2   2        24
                63.11         20.26        1.4732    5   1   1        24
                63.11          6.86        1.4732    3   3   3         8
                69.46         20.10        1.3532    4   4   0        12
                79.13          5.75        1.2104    6   2   0        24
                82.66          8.05        1.1674    5   3   3        24
                83.83          6.00        1.1540    6   2   2        24
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.