Co0.2 Cr1.8 D3.56 Zr Soubeyroux J, Bououdina M, Fruchart D, Pontonnier L Journal of Alloys and Compounds 219 (1995) 48-54 Phase stability and neutron diffraction studies of Laves phases Zr (Cr1-x Mx)2 with M =Mn,Fe,Co,Ni,Cu and 0 < x <0.2 and their hydrides _cod_database_code 1008688 _database_code_amcsd 0016574 CELL PARAMETERS: 7.6605 7.6605 7.6605 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 449.543 Density (g/cm3): 5.915 MAX. ABS. INTENSITY / VOLUME**2: 167.3893102 RIR: 9.215 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.08 1.23 4.4228 1 1 1 8 33.07 46.20 2.7084 2 2 0 12 39.00 100.00 2.3097 3 1 1 24 40.80 24.29 2.2114 2 2 2 8 59.08 15.48 1.5637 4 2 2 24 63.06 20.28 1.4743 5 1 1 24 63.06 6.85 1.4743 3 3 3 8 69.40 20.15 1.3542 4 4 0 12 79.06 5.72 1.2112 6 2 0 24 82.59 8.06 1.1682 5 3 3 24 83.76 6.05 1.1549 6 2 2 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.