Ba2 Ga Ge N Clarke S, DiSalvo F Journal of Alloys and Compounds 259 (1997) 158-162 Synthesis and structure of the subnitrides Ba2GeGaN and (Bax Sr1-x)3Ge2N2; x = 0.7 _cod_database_code 1005040 _database_code_amcsd 0012795 CELL PARAMETERS: 7.2490 4.2100 9.3140 90.000 108.870 90.000 SPACE GROUP: P2_1/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 268.970 Density (g/cm3): 5.321 MAX. ABS. INTENSITY / VOLUME**2: 47.02985835 RIR: 2.878 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.04 3.18 8.8134 0 0 1 2 12.91 2.16 6.8594 1 0 0 2 13.55 6.49 6.5333 -1 0 1 2 23.42 5.06 3.7988 0 1 1 4 24.62 3.69 3.6158 -2 0 1 2 24.81 58.10 3.5881 1 1 0 4 25.98 36.87 3.4297 2 0 0 2 27.30 84.32 3.2667 -2 0 2 2 27.37 72.27 3.2591 1 0 2 2 28.40 16.04 3.1427 1 1 1 4 28.93 3.06 3.0858 -1 0 3 2 29.32 99.17 3.0461 -1 1 2 4 29.34 100.00 3.0441 0 1 2 4 30.43 34.08 2.9378 0 0 3 2 30.88 9.17 2.8954 2 0 1 2 32.65 12.92 2.7430 -2 1 1 4 33.12 11.94 2.7049 -2 0 3 2 33.71 72.20 2.6590 2 1 0 4 34.76 33.04 2.5809 -2 1 2 4 34.81 24.64 2.5771 1 1 2 4 36.09 24.12 2.4888 -1 1 3 4 37.32 1.72 2.4092 0 1 3 4 37.71 16.83 2.3856 2 1 1 4 38.67 36.57 2.3285 -1 0 4 2 39.41 15.93 2.2865 3 0 0 2 39.60 5.22 2.2757 -2 1 3 4 40.90 1.36 2.2065 -2 0 4 2 41.46 3.24 2.1778 -3 0 3 2 42.96 5.45 2.1052 1 1 3 4 42.97 48.57 2.1050 0 2 0 2 43.25 7.48 2.0921 -3 1 1 4 43.89 13.20 2.0628 -3 1 2 4 43.96 11.83 2.0597 2 1 2 4 45.12 17.44 2.0093 3 1 0 4 46.47 1.58 1.9543 -2 1 4 4 46.77 6.29 1.9423 2 0 3 2 47.12 2.37 1.9285 -3 0 4 2 47.23 1.35 1.9244 1 0 4 2 49.02 1.35 1.8582 -1 0 5 2 49.94 9.24 1.8262 -2 0 5 2 50.48 10.25 1.8079 -4 0 2 2 50.57 6.34 1.8049 3 0 2 2 50.85 2.45 1.7957 -4 0 1 2 50.90 10.08 1.7940 2 2 0 4 51.66 26.31 1.7694 -2 2 2 4 51.70 22.66 1.7682 1 2 2 4 51.84 18.16 1.7636 2 1 3 4 51.87 1.51 1.7627 0 0 5 2 52.17 12.62 1.7533 -3 1 4 4 52.27 7.91 1.7502 1 1 4 4 52.63 1.06 1.7389 -1 2 3 4 53.56 12.61 1.7111 0 2 3 4 53.85 3.22 1.7026 2 2 1 4 53.93 9.60 1.7000 -1 1 5 4 55.30 5.00 1.6612 -2 2 3 4 55.30 4.37 1.6612 -4 1 2 4 55.39 2.92 1.6589 3 1 2 4 55.65 2.23 1.6517 -4 1 1 4 56.33 2.04 1.6333 -4 0 4 2 56.47 1.21 1.6295 2 0 4 2 56.61 13.56 1.6259 0 1 5 4 57.07 15.54 1.6139 -4 1 3 4 58.02 6.15 1.5897 4 0 1 2 58.08 11.28 1.5882 4 1 0 4 58.09 7.21 1.5879 1 0 5 2 59.08 14.97 1.5635 -3 1 5 4 59.17 18.37 1.5615 -1 2 4 4 59.71 8.22 1.5486 3 2 0 4 59.96 1.26 1.5429 -2 0 6 2 59.99 1.22 1.5421 -1 0 6 2 60.83 5.60 1.5228 -4 1 4 4 60.97 1.53 1.5197 2 1 4 4 61.24 1.89 1.5135 -3 2 3 4 62.12 3.12 1.4942 -4 0 5 2 62.45 1.36 1.4872 4 1 1 4 62.51 7.06 1.4857 1 1 5 4 63.04 8.47 1.4746 3 1 3 4 63.21 1.23 1.4710 -3 0 6 2 64.25 1.88 1.4497 -5 0 2 2 64.30 1.15 1.4487 -2 1 6 4 64.35 1.82 1.4477 4 0 2 2 65.37 1.43 1.4275 -5 0 1 2 65.38 4.18 1.4275 2 2 3 4 65.66 1.54 1.4220 -3 2 4 4 67.44 2.10 1.3887 -3 1 6 4 67.54 1.01 1.3869 0 1 6 4 67.96 6.52 1.3794 -2 2 5 4 68.21 2.94 1.3749 1 3 0 4 68.38 2.75 1.3719 5 0 0 2 68.40 7.43 1.3715 -4 2 2 4 68.45 4.42 1.3707 -5 1 2 4 68.48 4.63 1.3702 3 2 2 4 68.54 2.42 1.3690 4 1 2 4 68.71 1.70 1.3661 -4 2 1 4 69.56 1.13 1.3514 0 2 5 4 69.93 1.06 1.3452 1 3 1 4 70.40 6.25 1.3373 -1 3 2 4 70.41 6.29 1.3372 0 3 2 4 71.21 1.36 1.3242 2 1 5 4 71.70 5.12 1.3163 -1 0 7 2 71.89 2.36 1.3134 -5 1 4 4 72.05 1.18 1.3107 3 1 4 4 72.21 1.10 1.3083 -2 3 1 4 72.31 3.39 1.3067 -5 0 5 2 72.82 6.22 1.2988 2 3 0 4 73.15 2.09 1.2938 -3 0 7 2 73.37 1.68 1.2904 -4 2 4 4 73.44 2.90 1.2894 -2 3 2 4 73.47 2.18 1.2889 1 3 2 4 74.24 2.31 1.2774 -1 3 3 4 74.85 5.12 1.2686 4 2 1 4 74.91 6.12 1.2677 1 2 5 4 74.92 5.25 1.2675 -2 1 7 4 75.25 1.73 1.2628 2 3 1 4 76.21 2.85 1.2493 4 1 3 4 76.56 1.07 1.2444 -2 2 6 4 76.59 1.02 1.2440 -1 2 6 4 77.12 2.14 1.2367 -3 1 7 4 78.34 1.59 1.2205 -4 0 7 2 78.50 2.90 1.2184 -4 2 5 4 78.50 5.38 1.2184 3 0 5 2 79.39 1.91 1.2070 -3 3 2 4 79.44 1.70 1.2064 2 3 2 4 79.45 1.73 1.2063 0 1 7 4 79.49 1.16 1.2058 -3 2 6 4 79.52 1.26 1.2054 -6 0 2 2 79.53 1.29 1.2053 -6 0 3 2 79.63 1.02 1.2040 5 0 2 2 80.27 2.63 1.1960 3 3 0 4 80.44 1.84 1.1939 -5 2 2 4 80.53 1.77 1.1928 4 2 2 4 81.32 1.13 1.1832 -6 0 4 2 81.46 1.37 1.1815 -5 2 1 4 82.19 1.64 1.1728 1 0 7 2 82.40 1.27 1.1704 3 1 5 4 83.40 2.89 1.1588 -6 1 2 4 83.51 1.61 1.1576 5 1 2 4 84.25 2.91 1.1493 5 2 0 4 84.80 1.12 1.1432 6 0 0 2 84.86 1.60 1.1426 -6 0 5 2 85.33 3.47 1.1375 2 3 3 4 85.59 2.50 1.1347 -3 3 4 4 85.67 1.56 1.1339 1 3 4 4 86.05 4.91 1.1298 1 1 7 4 87.01 2.12 1.1199 -1 3 5 4 87.38 5.68 1.1160 -1 2 7 4 87.71 2.55 1.1127 5 0 3 2 87.96 3.75 1.1102 -5 2 5 4 88.20 1.39 1.1078 -3 1 8 4 88.28 1.37 1.1070 -1 1 8 4 88.65 4.06 1.1033 6 1 0 4 88.71 2.42 1.1027 -6 1 5 4 88.76 2.39 1.1022 -3 2 7 4 89.21 3.24 1.0979 0 3 5 4 89.59 1.81 1.0942 -4 -3 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.