Fe6 Ge6 Hf Schobinger-Papamantellos P, Buschow K, de Boer F, Ritter C, Isnard O, Fauth F Journal of Alloys and Compounds 267 (1998) 59-65 The Fe ordering in R Fe6 Ge6 compounds with non-magnetic R (R = Y, Lu, Hf) studied by neutron diffraction and magnetic measurements _cod_database_code 1008889 _database_code_amcsd 0016756 CELL PARAMETERS: 5.0250 5.0250 8.0149 90.000 90.000 120.000 SPACE GROUP: P6/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 175.267 Density (g/cm3): 8.994 MAX. ABS. INTENSITY / VOLUME**2: 133.8501891 RIR: 4.846 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.04 15.14 8.0149 0 0 1 2 20.41 3.42 4.3518 1 0 0 6 23.26 14.84 3.8244 1 0 1 12 30.32 5.79 2.9479 1 0 2 12 33.54 11.29 2.6716 0 0 3 2 35.74 76.46 2.5125 1 1 0 6 37.51 4.19 2.3975 1 1 1 12 39.58 47.12 2.2768 1 0 3 12 41.50 52.45 2.1759 2 0 0 6 42.46 100.00 2.1287 1 1 2 12 43.08 3.12 2.0999 2 0 1 12 45.26 25.63 2.0037 0 0 4 2 47.55 37.93 1.9122 2 0 2 12 49.82 23.09 1.8303 1 1 3 12 50.12 8.00 1.8201 1 0 4 12 54.38 15.51 1.6871 2 0 3 12 57.17 2.08 1.6112 2 1 1 24 58.96 8.52 1.5666 1 1 4 12 61.66 1.54 1.5042 1 0 5 12 63.07 6.30 1.4740 2 0 4 12 64.21 12.33 1.4506 3 0 0 6 66.79 17.05 1.4007 2 1 3 24 68.83 19.94 1.3640 3 0 2 12 73.36 1.25 1.2906 2 0 5 12 74.27 4.15 1.2770 1 0 6 12 74.42 5.88 1.2748 3 0 3 12 74.66 4.34 1.2713 2 1 4 24 75.71 8.14 1.2563 2 2 0 6 81.63 22.43 1.1795 1 1 6 12 82.01 2.88 1.1750 3 0 4 12 84.37 1.01 1.1480 2 1 5 24 85.25 1.04 1.1384 2 0 6 12 85.39 1.15 1.1368 2 2 3 12 89.00 2.28 1.0999 3 1 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.