Diopside Gualtieri A F Journal of Applied Crystallography 33 (2000) 267-278 Accuracy of XRPD QPA using the combined Rietveld-RIR method Locality: Napoli, Italy _database_code_amcsd 0012864 CELL PARAMETERS: 9.7504 8.9015 5.2744 90.000 106.016 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 440.016 Density (g/cm3): 3.384 MAX. ABS. INTENSITY / VOLUME**2: 11.57521875 RIR: 1.114 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.72 2.32 6.4542 1 1 0 4 18.94 3.59 4.6860 2 0 0 2 19.95 6.32 4.4507 0 2 0 2 26.65 5.12 3.3447 0 2 1 4 27.64 34.90 3.2271 2 2 0 4 29.86 100.00 2.9921 -2 2 1 4 30.32 41.58 2.9477 3 1 0 4 30.87 25.80 2.8970 -3 1 1 4 35.01 36.05 2.5627 -1 3 1 4 35.41 35.85 2.5349 0 0 2 2 35.71 38.25 2.5145 2 2 1 4 38.42 1.08 2.3430 4 0 0 2 39.15 10.68 2.3012 3 1 1 4 40.64 8.52 2.2202 1 1 2 4 40.88 1.10 2.2076 -2 2 2 4 40.97 4.75 2.2027 0 2 2 4 42.00 9.61 2.1514 3 3 0 4 42.41 18.52 2.1314 -3 3 1 4 42.91 11.22 2.1077 -4 2 1 4 44.46 15.43 2.0377 0 4 1 4 44.85 12.54 2.0208 -4 0 2 2 45.12 9.12 2.0096 2 0 2 2 46.05 4.32 1.9712 -1 3 2 4 46.59 1.34 1.9494 -2 4 1 4 49.71 5.49 1.8342 5 1 0 4 49.78 3.52 1.8315 2 2 2 4 50.29 2.65 1.8142 1 3 2 4 50.80 1.44 1.7972 2 4 1 4 51.54 1.53 1.7733 4 2 1 4 52.31 13.00 1.7490 1 5 0 4 53.46 1.67 1.7140 3 1 2 4 54.62 1.18 1.6803 -1 5 1 4 54.90 3.56 1.6724 0 4 2 4 55.16 3.24 1.6650 -3 1 3 4 56.46 15.74 1.6297 -2 2 3 4 56.67 14.74 1.6242 -5 3 1 4 57.08 2.34 1.6136 4 4 0 4 59.15 3.53 1.5620 6 0 0 2 59.79 4.57 1.5468 3 5 0 4 60.43 3.61 1.5319 -6 0 2 2 60.70 2.01 1.5257 -6 2 1 4 60.79 6.68 1.5237 4 0 2 2 61.53 10.31 1.5071 -1 3 3 4 62.62 4.29 1.4836 0 6 0 2 63.77 1.09 1.4595 4 4 1 4 64.31 1.73 1.4485 -6 2 2 4 65.71 16.41 1.4211 5 3 1 4 66.36 7.27 1.4087 -3 5 2 4 66.49 2.84 1.4061 1 5 2 4 66.81 1.87 1.4003 1 3 3 4 67.24 3.36 1.3923 2 2 3 4 68.13 1.64 1.3763 -2 4 3 4 69.89 1.01 1.3458 0 4 3 4 70.61 1.01 1.3339 2 6 1 4 70.72 5.22 1.3321 -7 1 2 4 71.11 2.51 1.3258 6 2 1 4 71.49 3.73 1.3197 -5 3 3 4 73.21 3.52 1.2929 -3 1 4 4 73.97 1.57 1.2814 -2 6 2 4 74.04 4.67 1.2804 0 6 2 4 74.67 1.90 1.2712 -4 0 4 2 74.93 2.75 1.2674 0 0 4 2 76.39 6.44 1.2468 3 5 2 4 78.97 1.30 1.2124 1 7 1 4 84.02 2.06 1.1519 -6 0 4 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.