Illite Gualtieri A F Journal of Applied Crystallography 33 (2000) 267-278 Accuracy of XRPD QPA using the combined Rietveld-RIR method Locality: Napoli, Italy _database_code_amcsd 0012865 CELL PARAMETERS: 5.2226 9.0183 20.1430 90.000 95.665 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 944.081 Density (g/cm3): 2.780 MAX. ABS. INTENSITY / VOLUME**2: 3.985989115 RIR: 0.467 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 8.82 57.21 10.0223 0 0 2 2 17.70 35.02 5.0112 0 0 4 2 19.69 6.65 4.5092 0 2 0 2 19.72 26.97 4.5029 1 1 0 4 19.84 100.00 4.4760 -1 1 1 4 20.19 23.41 4.3992 0 2 1 4 20.58 10.88 4.3152 1 1 1 4 20.92 3.06 4.2454 -1 1 2 4 21.61 13.24 4.1121 0 2 2 4 22.33 13.53 3.9820 1 1 2 4 22.85 31.08 3.8915 -1 1 3 4 23.81 38.42 3.7376 0 2 3 4 24.77 10.25 3.5943 1 1 3 4 25.44 65.45 3.5015 -1 1 4 4 26.59 49.14 3.3519 0 2 4 4 26.68 53.87 3.3408 0 0 6 2 27.74 71.43 3.2154 1 1 4 4 28.52 33.96 3.1301 -1 1 5 4 29.82 54.28 2.9960 0 2 5 4 31.11 33.04 2.8746 1 1 5 4 31.96 24.83 2.8000 -1 1 6 4 34.47 3.24 2.6022 1 3 0 4 34.52 14.99 2.5985 2 0 0 2 34.54 38.95 2.5969 -1 3 1 4 34.78 11.52 2.5795 1 1 6 4 34.80 48.16 2.5780 -2 0 2 2 34.99 57.37 2.5644 1 3 1 4 35.69 5.66 2.5157 -1 1 7 4 35.84 8.83 2.5056 0 0 8 2 36.43 10.43 2.4663 -1 3 3 4 36.57 8.98 2.4571 2 0 2 2 37.20 5.15 2.4173 0 2 7 4 37.38 24.26 2.4059 -2 0 4 2 37.71 30.65 2.3852 1 3 3 4 38.17 3.03 2.3575 -1 3 4 4 38.68 1.70 2.3278 1 1 7 4 39.91 6.92 2.2589 -2 2 1 4 39.99 5.30 2.2546 0 4 0 2 40.25 3.49 2.2404 0 4 1 4 40.38 3.91 2.2337 -1 3 5 4 40.66 3.11 2.2191 2 0 4 2 40.71 2.12 2.2164 2 2 1 4 41.03 1.20 2.1996 0 4 2 4 41.20 12.63 2.1910 -2 2 3 4 41.22 2.27 2.1902 0 2 8 4 41.87 6.35 2.1576 2 2 2 4 41.88 7.68 2.1569 -2 0 6 2 42.31 1.38 2.1362 0 4 3 4 42.33 24.23 2.1350 1 3 5 4 42.78 2.29 2.1140 1 1 8 4 43.50 7.88 2.0804 2 2 3 4 43.78 1.02 2.0679 -1 1 9 4 44.04 4.94 2.0561 0 4 4 4 45.24 26.10 2.0045 0 0 10 2 45.95 13.54 1.9750 -1 3 7 4 46.20 1.93 1.9651 0 4 5 4 46.34 5.27 1.9595 2 0 6 2 46.68 4.86 1.9457 -2 2 6 4 48.01 1.04 1.8951 2 2 5 4 48.08 3.21 1.8923 -1 1 10 4 48.42 2.45 1.8801 1 3 7 4 48.73 4.80 1.8688 0 4 6 4 49.22 1.15 1.8512 -1 3 8 4 52.25 2.76 1.7508 -2 2 8 4 52.76 4.30 1.7349 -1 3 9 4 53.23 7.16 1.7208 2 0 8 2 53.80 5.85 1.7040 1 5 0 4 53.83 1.72 1.7029 2 4 0 4 53.89 2.78 1.7013 3 1 0 4 54.17 2.36 1.6932 1 5 1 4 54.34 7.27 1.6883 -3 1 3 4 54.36 2.28 1.6876 2 4 1 4 54.58 1.74 1.6815 3 1 1 4 54.76 1.74 1.6763 -2 4 3 4 54.95 1.39 1.6709 1 5 2 4 55.03 15.84 1.6688 -2 0 10 2 55.30 1.37 1.6612 2 4 2 4 55.32 1.44 1.6607 -3 1 4 4 55.50 1.96 1.6557 -2 2 9 4 55.63 23.47 1.6522 1 3 9 4 55.67 1.73 1.6511 3 1 2 4 55.89 1.50 1.6451 -2 4 4 4 56.48 9.41 1.6294 -1 5 4 4 56.63 2.75 1.6252 2 4 3 4 56.69 4.26 1.6237 -3 1 5 4 57.15 5.25 1.6117 3 1 3 4 57.15 2.13 1.6117 -1 1 12 4 57.40 1.08 1.6052 -2 4 5 4 57.71 3.40 1.5976 1 5 4 4 58.44 3.94 1.5792 -3 1 6 4 59.01 6.41 1.5654 3 1 4 4 59.02 1.60 1.5651 -2 2 10 4 59.29 4.56 1.5585 -2 4 6 4 60.16 2.22 1.5382 -1 5 6 4 60.58 7.92 1.5286 -1 3 11 4 61.11 5.86 1.5164 2 0 10 2 61.56 25.31 1.5064 -3 3 1 4 61.71 14.14 1.5030 0 6 0 2 61.91 1.32 1.4988 0 6 1 4 61.93 1.54 1.4984 1 5 6 4 62.22 1.87 1.4920 -3 3 3 4 62.44 1.21 1.4873 3 3 1 4 62.48 2.21 1.4864 0 6 2 4 62.80 1.92 1.4797 -2 2 11 4 62.83 1.20 1.4790 2 4 6 4 63.79 1.80 1.4591 1 3 11 4 63.80 2.76 1.4590 0 2 13 4 64.54 1.47 1.4439 1 5 7 4 64.87 1.47 1.4373 2 2 10 4 65.16 2.75 1.4318 0 0 14 2 65.66 2.62 1.4219 1 1 13 4 68.61 1.22 1.3678 3 3 5 4 69.02 2.11 1.3607 2 2 11 4 69.28 11.46 1.3562 -1 3 13 4 69.89 7.97 1.3460 2 0 12 2 70.11 2.31 1.3422 0 4 12 4 70.73 3.58 1.3319 1 1 14 4 71.09 3.06 1.3261 -2 2 13 4 71.50 2.49 1.3195 -1 5 10 4 71.97 3.34 1.3121 -1 1 15 4 72.11 1.07 1.3098 -2 0 14 2 72.42 2.50 1.3050 -4 0 2 2 72.58 2.25 1.3025 -2 6 1 4 72.67 3.95 1.3011 2 6 0 4 72.79 2.43 1.2993 4 0 0 2 72.83 1.45 1.2987 1 3 13 4 72.84 7.22 1.2985 -2 6 2 4 72.93 4.93 1.2972 -3 3 9 4 73.47 3.98 1.2889 0 6 8 4 73.73 2.11 1.2850 3 3 7 4 74.42 4.58 1.2747 -2 6 4 4 74.56 2.13 1.2727 0 4 13 4 74.57 2.35 1.2726 4 0 2 2 75.60 1.06 1.2579 -2 2 14 4 75.74 1.49 1.2559 -2 6 5 4 75.91 1.11 1.2535 -4 2 1 4 75.91 2.33 1.2534 -4 0 6 2 76.16 2.58 1.2499 -1 7 1 4 76.56 3.14 1.2445 2 6 4 4 76.57 1.27 1.2442 -3 5 3 4 77.69 1.64 1.2291 3 5 2 4 77.96 1.22 1.2255 -4 2 5 4 78.08 1.07 1.2239 1 7 3 4 79.75 1.87 1.2025 0 6 10 4 80.06 1.08 1.1986 -3 5 6 4 80.10 1.20 1.1981 3 3 9 4 80.55 1.71 1.1925 3 5 4 4 80.97 1.36 1.1874 3 1 11 4 81.10 2.02 1.1858 1 7 5 4 85.28 1.78 1.1380 3 1 12 4 86.42 1.14 1.1260 -4 4 3 4 87.30 5.07 1.1168 -2 6 10 4 88.03 2.78 1.1095 4 0 8 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.