CoCr2S4 Raccah P M, Bouchard R J, Wold A Journal of Applied Physics 37 (1966) 1436-1437 Locality: synthetic Crystallographic study of chromium spinels _database_code_amcsd 0012906 CELL PARAMETERS: 9.9230 9.9230 9.9230 90.000 90.000 90.000 SPACE GROUP: Fd-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 977.078 Density (g/cm3): 3.958 MAX. ABS. INTENSITY / VOLUME**2: 49.21913431 RIR: 4.049 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.47 7.98 5.7290 1 1 1 8 25.39 34.03 3.5083 2 2 0 12 29.86 100.00 2.9919 3 1 1 24 31.22 1.62 2.8645 2 2 2 8 36.21 47.65 2.4808 4 0 0 6 44.74 12.39 2.0255 4 2 2 24 47.62 36.62 1.9097 5 1 1 24 47.62 4.76 1.9097 3 3 3 8 52.14 82.42 1.7542 4 4 0 12 58.86 4.55 1.5690 6 2 0 24 61.25 10.01 1.5132 5 3 3 24 65.13 7.83 1.4323 4 4 4 8 67.40 1.17 1.3895 5 5 1 24 71.10 5.55 1.3260 6 4 2 48 73.27 7.80 1.2919 5 5 3 24 73.27 6.13 1.2919 7 3 1 48 76.85 10.23 1.2404 8 0 0 6 82.48 1.58 1.1694 8 2 2 24 82.48 1.00 1.1694 6 6 0 12 84.57 6.40 1.1458 7 5 1 48 84.57 2.33 1.1458 5 5 5 8 88.04 8.71 1.1094 8 4 0 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.