CdCr2O4 Raccah P M, Bouchard R J, Wold A Journal of Applied Physics 37 (1966) 1436-1437 Locality: synthetic Crystallographic study of chromium spinels _database_code_amcsd 0012912 CELL PARAMETERS: 8.5960 8.5960 8.5960 90.000 90.000 90.000 SPACE GROUP: Fd-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 635.169 Density (g/cm3): 5.864 MAX. ABS. INTENSITY / VOLUME**2: 145.3669452 RIR: 8.072 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.87 2.33 4.9629 1 1 1 8 29.39 61.51 3.0391 2 2 0 12 34.61 100.00 2.5918 3 1 1 24 36.20 3.59 2.4815 2 2 2 8 42.04 2.20 2.1490 4 0 0 6 46.02 3.81 1.9721 3 3 1 24 52.13 19.87 1.7547 4 2 2 24 55.55 28.75 1.6543 5 1 1 24 55.55 5.30 1.6543 3 3 3 8 60.97 32.32 1.5196 4 4 0 12 69.11 6.97 1.3591 6 2 0 24 72.04 8.85 1.3109 5 3 3 24 73.01 1.99 1.2959 6 2 2 24 84.31 8.52 1.1487 6 4 2 48 87.08 5.76 1.1191 5 5 3 24 87.08 7.58 1.1191 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.