Zinc
      Jette E R, Foote F
      Journal of Chemical Physics 3 (1935) 605-616
      Precision determination of lattice constants
      Locality: synthetic
      Sample: at T = 25 C
      Note: lattice parameter is average of three samples
      _database_code_amcsd 0012940

      CELL PARAMETERS:    2.6594   2.6594   4.9368   90.000   90.000  120.000
      SPACE GROUP: P6_3/mmc  
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     30.237
      Density (g/cm3):      7.183
      MAX. ABS. INTENSITY / VOLUME**2:      228.7907827    
      RIR:     10.371
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                36.40         37.54        2.4684    0   0   2         2
                39.11         22.80        2.3031    1   0   0         6
                43.35        100.00        2.0872    1   0   1        12
                54.49         15.81        1.6839    1   0   2        12
                70.31         19.40        1.3389    1   0   3        12
                70.87         12.58        1.3297    1   1   0         6
                77.31          3.11        1.2342    0   0   4         2
                82.38         15.25        1.1707    1   1   2        12
                84.05          1.79        1.1516    2   0   0         6
                86.85          9.79        1.1214    2   0   1        12
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.