LiAlO2
      Marezio M, Remeika J P
      Journal of Chemical Physics 44 (1966) 3143-3144
      High-pressure synthesis and crystal structure of alpha-LiAlO2
      _database_code_amcsd 0012984

      CELL PARAMETERS:    2.8003   2.8003  14.2160   90.000   90.000  120.000
      SPACE GROUP: R-3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     96.542
      Density (g/cm3):      3.401
      MAX. ABS. INTENSITY / VOLUME**2:      21.21414810    
      RIR:      2.031
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.73         98.11        4.7387    0   0   3         2
                37.63         18.05        2.3906    1   0   1         6
                45.27        100.00        2.0032    1   0   4         6
                49.39          2.50        1.8451    0   1   5         6
                59.36         14.44        1.5570    1   0   7         6
                65.07         22.49        1.4334    0   1   8         6
                66.82         24.15        1.4001    1   1   0         6
                70.08         10.01        1.3428    1   1   3        12
                77.89          1.19        1.2264    1   0  10         6
                79.30          1.86        1.2082    0   2   1         6
                79.52          1.28        1.2054    1   1   6        12
                81.20          2.70        1.1847    0   0  12         2
                84.41          9.91        1.1476    0   2   4         6
                85.05          5.34        1.1405    0   1  11         6
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.