Gd0.07 O3 Ta0.21 W0.79 Desgardin G, Raveau B Journal of Inorganic and Nuclear Chemistry 34 (1972) 509-516 Sur de nouvelles phases non stoechiometriques de type Perovskite Gdx(Ta3x W1-3x) O3 _cod_database_code 1001056 _database_code_amcsd 0013029 CELL PARAMETERS: 5.3260 5.3830 3.7860 90.000 90.000 90.000 SPACE GROUP: Cmmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 108.544 Density (g/cm3): 7.411 MAX. ABS. INTENSITY / VOLUME**2: 436.6592244 RIR: 19.186 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.50 66.67 3.7860 1 1 0 4 23.50 33.33 3.7860 0 0 1 2 33.29 11.64 2.6915 0 2 0 2 33.47 45.87 2.6771 1 1 1 8 33.66 11.30 2.6630 2 0 0 2 41.15 6.41 2.1937 0 2 1 4 41.46 6.29 2.1781 2 0 1 4 48.06 14.33 1.8930 2 2 0 4 48.06 7.16 1.8930 0 0 2 2 53.92 6.12 1.7004 1 3 0 4 54.17 12.04 1.6932 2 2 1 8 54.17 12.04 1.6932 1 1 2 8 54.42 5.93 1.6860 3 1 0 4 59.60 8.17 1.5512 1 3 1 8 59.72 4.06 1.5484 0 2 2 4 59.95 4.01 1.5429 2 0 2 4 60.07 7.96 1.5402 3 1 1 8 69.90 1.92 1.3457 0 4 0 2 70.33 7.53 1.3386 2 2 2 8 70.76 1.84 1.3315 4 0 0 2 74.89 2.00 1.2680 0 4 1 4 75.10 3.96 1.2650 1 3 2 8 75.30 1.96 1.2620 3 3 0 4 75.51 3.89 1.2590 3 1 2 8 75.72 1.93 1.2561 4 0 1 4 79.86 1.58 1.2011 2 4 0 4 80.17 3.12 1.1973 3 3 1 8 80.17 3.12 1.1972 1 1 3 8 80.48 1.54 1.1934 4 2 0 4 84.66 1.60 1.1449 2 4 1 8 85.27 1.58 1.1382 4 2 1 8 89.31 1.77 1.0968 0 4 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.