ZnFeF5(H2O)2 Laligant Y, Calage Y, Torres Tapia E, Greneche J, Varret F, Ferey G Journal of Magnetism and Magnetic Materials 61 (1986) 283-290 Crystal structure of the inverse weberite ZnFeF5(H2O)2, magnetic and Mossbauer study of the antiferromagnet ZnFeF5(H2O)2 and ferrimagnet MnFeF5 _cod_database_code 1000247 _database_code_amcsd 0013056 CELL PARAMETERS: 7.4750 10.7660 6.5940 90.000 90.000 90.000 SPACE GROUP: Imma X-RAY WAVELENGTH: 1.541838 Cell Volume: 530.658 Density (g/cm3): 3.211 MAX. ABS. INTENSITY / VOLUME**2: 23.39412145 RIR: 2.372 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.76 100.00 5.6231 0 1 1 4 16.47 4.02 5.3830 0 2 0 2 17.94 57.30 4.9450 1 0 1 4 24.44 56.09 3.6416 1 2 1 8 27.04 1.91 3.2970 0 0 2 2 28.31 37.62 3.1521 0 3 1 4 28.68 39.46 3.1127 2 1 1 8 29.09 69.44 3.0701 2 2 0 4 31.83 37.67 2.8116 0 2 2 4 33.29 5.60 2.6915 0 4 0 2 36.34 2.19 2.4725 2 0 2 4 38.07 5.35 2.3640 1 4 1 8 39.01 8.44 2.3092 1 3 2 8 41.34 10.25 2.1841 2 4 0 4 42.25 11.62 2.1389 3 2 1 8 42.89 22.41 2.1087 1 0 3 4 43.40 3.18 2.0850 0 4 2 4 46.24 11.06 1.9634 1 2 3 8 46.45 1.54 1.9548 3 1 2 8 48.57 11.61 1.8744 0 3 3 4 48.73 17.07 1.8687 4 0 0 2 48.81 1.73 1.8660 2 1 3 8 50.10 39.36 1.8208 2 4 2 8 50.86 5.76 1.7953 2 5 1 8 51.53 4.90 1.7734 4 1 1 8 51.89 16.96 1.7620 3 4 1 8 54.39 8.35 1.6867 1 6 1 8 54.79 4.92 1.6755 2 3 3 8 55.35 5.46 1.6599 1 4 3 8 55.76 5.48 1.6485 0 0 4 2 55.77 4.02 1.6483 3 0 3 4 56.93 3.22 1.6176 2 6 0 4 57.32 9.38 1.6075 4 3 1 8 58.57 4.88 1.5761 3 2 3 8 58.57 10.28 1.5760 0 6 2 4 59.38 10.54 1.5563 4 2 2 8 60.16 2.07 1.5381 0 5 3 4 60.29 5.53 1.5350 4 4 0 4 61.96 3.15 1.4978 0 7 1 4 63.84 3.75 1.4580 5 0 1 4 64.12 12.00 1.4524 2 2 4 8 64.13 1.39 1.4522 2 6 2 8 65.64 5.82 1.4224 2 5 3 8 65.67 4.60 1.4218 3 6 1 8 66.43 2.70 1.4073 5 2 1 8 66.51 2.75 1.4058 0 4 4 4 66.52 6.78 1.4057 3 4 3 8 67.35 1.04 1.3903 2 7 1 8 69.90 3.07 1.3457 0 8 0 2 71.26 3.13 1.3234 4 3 3 8 72.16 1.51 1.3090 0 1 5 4 72.84 3.32 1.2985 1 8 1 8 73.81 2.34 1.2838 3 3 4 8 74.54 1.25 1.2730 5 3 2 8 75.27 1.02 1.2625 1 2 5 8 76.45 1.09 1.2460 0 8 2 4 77.16 2.85 1.2362 4 0 4 4 77.16 3.50 1.2362 5 0 3 4 77.22 3.16 1.2354 2 1 5 8 78.86 2.78 1.2138 6 2 0 4 79.56 1.72 1.2048 5 2 3 8 79.57 6.89 1.2048 4 6 2 8 81.42 3.24 1.1820 2 8 2 8 81.84 1.23 1.1770 0 9 1 4 82.46 1.12 1.1697 1 4 5 8 82.54 1.70 1.1687 4 7 1 8 82.83 1.43 1.1654 6 0 2 4 83.78 4.00 1.1546 2 6 4 8 85.62 1.00 1.1344 1 8 3 8 85.89 1.57 1.1315 5 6 1 8 86.67 2.93 1.1234 4 4 4 8 89.81 1.55 1.0921 4 8 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.