Barioferrite Collomb A, Wolfers P, Obradors X Journal of Magnetism and Magnetic Materials 62 (1986) 57-67 Neutron diffraction studies of some hexagonal ferrites: BaFe12O19, BaMg2-W and CaCo2-W Note: T = 470 C, neutron, refined with MXD Locality: synthetic _database_code_amcsd 0013057 CELL PARAMETERS: 5.9290 5.9290 23.4130 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 712.772 Density (g/cm3): 5.178 MAX. ABS. INTENSITY / VOLUME**2: 41.13525406 RIR: 2.587 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.68 6.22 5.0155 1 0 1 12 18.87 11.07 4.7022 1 0 2 12 22.79 9.55 3.9022 0 0 6 2 23.04 2.69 3.8600 1 0 4 12 28.73 1.46 3.1068 1 0 6 12 30.15 44.91 2.9645 1 1 0 6 30.55 15.17 2.9266 0 0 8 2 31.12 8.34 2.8738 1 1 2 12 31.93 89.72 2.8026 1 0 7 12 33.90 100.00 2.6446 1 1 4 12 34.95 9.48 2.5673 2 0 0 6 35.17 6.94 2.5520 2 0 1 12 35.30 7.85 2.5426 1 0 8 12 35.81 1.40 2.5077 2 0 2 12 36.86 46.87 2.4388 2 0 3 12 38.12 3.95 2.3606 1 1 6 12 38.81 1.60 2.3206 1 0 9 12 40.05 27.70 2.2512 2 0 5 12 42.13 17.20 2.1448 2 0 6 12 42.43 1.50 2.1303 1 0 10 12 46.17 4.70 1.9662 1 0 11 12 49.62 1.97 1.8374 1 1 10 12 49.91 6.91 1.8273 2 0 9 12 52.93 3.43 1.7300 2 0 10 12 53.54 6.97 1.7116 3 0 0 6 54.16 1.41 1.6935 3 0 2 12 54.68 34.84 1.6786 2 1 7 24 54.90 5.79 1.6724 0 0 14 2 55.98 19.18 1.6428 3 0 4 12 56.13 40.57 1.6386 2 0 11 12 56.46 3.42 1.6298 1 1 12 12 56.93 5.42 1.6174 2 1 8 24 59.51 2.60 1.5534 2 0 12 12 62.16 1.20 1.4934 1 0 15 12 62.68 40.52 1.4822 2 2 0 6 63.05 3.52 1.4744 2 0 13 12 65.04 2.58 1.4341 2 1 11 24 66.76 10.63 1.4013 2 0 14 12 67.61 1.82 1.3857 2 2 6 12 71.32 5.42 1.3223 2 2 8 12 71.96 2.27 1.3122 1 1 16 12 72.08 11.41 1.3103 3 1 7 24 73.62 1.24 1.2867 3 0 12 12 74.03 1.50 1.2805 3 1 8 24 74.98 4.14 1.2666 4 0 3 12 75.38 2.50 1.2609 1 0 18 12 77.03 2.06 1.2380 4 0 5 12 78.43 1.32 1.2194 4 0 6 12 78.67 1.05 1.2163 2 1 15 24 78.87 1.39 1.2136 2 0 17 12 80.67 4.01 1.1911 1 1 18 12 81.28 1.15 1.1836 3 1 11 24 82.38 1.18 1.1707 0 0 20 2 87.76 1.15 1.1122 3 0 16 12 87.87 1.75 1.1111 3 2 7 24 88.05 6.62 1.1093 2 2 14 12 88.94 2.56 1.1005 4 1 4 24 89.07 7.49 1.0992 4 0 11 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.