Barioferrite Collomb A, Wolfers P, Obradors X Journal of Magnetism and Magnetic Materials 62 (1986) 57-67 Neutron diffraction studies of some hexagonal ferrites: BaFe12O19, BaMg2-W and CaCo2-W Note: T = 4.2 K Locality: synthetic _database_code_amcsd 0013059 CELL PARAMETERS: 5.8650 5.8650 23.0990 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 688.113 Density (g/cm3): 5.364 MAX. ABS. INTENSITY / VOLUME**2: 43.78377247 RIR: 2.658 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.88 5.13 4.9607 1 0 1 12 19.09 10.99 4.6495 1 0 2 12 23.10 10.23 3.8498 0 0 6 2 23.32 2.75 3.8139 1 0 4 12 29.11 1.20 3.0681 1 0 6 12 30.48 45.32 2.9325 1 1 0 6 30.97 14.99 2.8874 0 0 8 2 31.47 8.79 2.8423 1 1 2 12 32.35 90.52 2.7672 1 0 7 12 34.30 100.00 2.6147 1 1 4 12 35.34 9.47 2.5396 2 0 0 6 35.56 6.77 2.5244 2 0 1 12 35.77 8.66 2.5101 1 0 8 12 36.22 1.31 2.4804 2 0 2 12 37.28 47.00 2.4118 2 0 3 12 38.59 2.91 2.3328 1 1 6 12 39.33 1.60 2.2907 1 0 9 12 40.53 26.67 2.2255 2 0 5 12 42.65 16.80 2.1199 2 0 6 12 43.02 1.39 2.1027 1 0 10 12 46.81 4.64 1.9406 1 0 11 12 47.53 1.19 1.9132 2 1 1 24 50.28 3.27 1.8146 1 1 10 12 50.56 6.42 1.8052 2 0 9 12 53.63 3.42 1.7088 2 0 10 12 54.17 7.30 1.6931 3 0 0 6 54.80 1.47 1.6752 3 0 2 12 55.37 36.30 1.6594 2 1 7 24 55.71 6.48 1.6499 0 0 14 2 56.65 19.42 1.6247 3 0 4 12 56.90 40.11 1.6183 2 0 11 12 57.25 3.97 1.6092 1 1 12 12 57.66 5.44 1.5987 2 1 8 24 60.20 1.09 1.5373 2 1 9 24 60.34 3.24 1.5341 2 0 12 12 63.08 1.22 1.4737 1 0 15 12 63.44 40.01 1.4662 2 2 0 6 63.95 2.93 1.4559 2 0 13 12 64.84 1.49 1.4380 1 1 14 12 65.93 3.11 1.4169 2 1 11 24 67.72 9.69 1.3836 2 0 14 12 68.47 1.90 1.3702 2 2 6 12 68.74 1.02 1.3655 3 0 10 12 69.10 1.05 1.3593 2 1 12 24 72.27 5.51 1.3073 2 2 8 12 73.03 12.68 1.2956 3 1 7 24 73.05 2.67 1.2952 1 1 16 12 74.66 1.48 1.2713 3 0 12 12 75.02 1.40 1.2661 3 1 8 24 75.95 4.36 1.2529 4 0 3 12 76.58 2.01 1.2442 1 0 18 12 78.05 2.03 1.2244 4 0 5 12 79.48 1.36 1.2059 4 0 6 12 79.85 1.15 1.2012 2 1 15 24 80.10 1.65 1.1981 2 0 17 12 81.95 5.45 1.1756 1 1 18 12 82.44 1.45 1.1699 3 1 11 24 83.75 1.38 1.1550 0 0 20 2 89.11 2.04 1.0988 3 2 7 24 89.14 1.38 1.0985 3 0 16 12 89.40 7.71 1.0960 2 2 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.