Barioferrite Collomb A, Wolfers P, Obradors X Journal of Magnetism and Magnetic Materials 62 (1986) 57-67 Neutron diffraction studies of some hexagonal ferrites: BaFe12O19, BaMg2-W and CaCo2-W Note: T = 4.2 K Sample: BaMg2 - W Locality: synthetic _database_code_amcsd 0013060 CELL PARAMETERS: 5.8920 5.8920 32.8500 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 987.624 Density (g/cm3): 5.089 MAX. ABS. INTENSITY / VOLUME**2: 33.78026526 RIR: 2.161 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 5.38 12.86 16.4250 0 0 2 2 17.38 1.09 5.1026 1 0 0 6 18.21 10.60 4.8729 1 0 2 12 19.19 8.01 4.6251 1 0 3 12 21.64 6.54 4.1062 0 0 8 2 27.15 9.50 3.2850 0 0 10 2 30.10 20.45 2.9687 1 0 9 12 30.34 49.12 2.9460 1 1 0 6 30.84 3.52 2.8997 1 1 2 12 32.28 13.16 2.7730 1 1 4 12 32.41 60.84 2.7621 1 0 10 12 32.71 7.94 2.7375 0 0 12 2 34.57 100.00 2.5943 1 1 6 12 34.81 38.27 2.5774 1 0 11 12 35.28 15.64 2.5437 2 0 1 12 35.61 4.95 2.5211 2 0 2 12 36.15 8.37 2.4848 2 0 3 12 36.89 27.66 2.4364 2 0 4 12 37.58 5.65 2.3937 1 1 8 12 37.83 11.59 2.3783 2 0 5 12 38.95 12.36 2.3126 2 0 6 12 40.23 2.15 2.2415 2 0 7 12 41.68 24.17 2.1671 2 0 8 12 42.40 2.80 2.1318 1 0 14 12 43.27 14.67 2.0911 2 0 9 12 45.22 1.45 2.0054 1 1 12 12 46.83 1.01 1.9398 2 0 11 12 47.75 3.46 1.9047 1 0 16 12 48.79 1.44 1.8664 2 0 12 12 49.67 1.31 1.8354 1 1 14 12 50.50 2.32 1.8071 1 0 17 12 50.86 4.02 1.7954 2 0 13 12 53.02 3.63 1.7271 2 0 14 12 53.76 7.74 1.7052 2 1 9 24 53.90 8.08 1.7009 3 0 0 6 54.47 2.05 1.6844 1 1 16 12 55.14 2.43 1.6655 3 0 4 12 55.23 21.49 1.6632 2 1 10 24 55.28 16.68 1.6618 2 0 15 12 55.99 6.16 1.6425 0 0 20 2 56.67 20.48 1.6243 3 0 6 12 56.83 18.34 1.6201 2 1 11 24 57.63 21.54 1.5995 2 0 16 12 58.76 1.33 1.5714 3 0 8 12 59.09 1.53 1.5635 1 0 20 12 59.59 1.55 1.5514 1 1 18 12 60.06 7.99 1.5404 2 0 17 12 62.32 2.34 1.4899 2 1 14 24 62.58 5.85 1.4843 2 0 18 12 63.12 48.30 1.4730 2 2 0 6 65.18 9.67 1.4313 2 0 19 12 66.52 2.12 1.4057 2 1 16 24 67.56 1.16 1.3865 2 2 8 12 67.86 1.79 1.3811 2 0 20 12 68.77 1.99 1.3651 2 1 17 24 70.00 2.64 1.3441 2 2 10 12 70.63 2.08 1.3336 2 0 21 12 70.74 2.35 1.3319 1 1 22 12 71.50 2.29 1.3195 3 1 9 24 72.76 8.43 1.2997 3 1 10 24 72.93 3.60 1.2971 2 2 12 12 74.14 5.83 1.2789 3 1 11 24 74.43 1.45 1.2747 4 0 1 12 74.58 1.77 1.2725 1 0 25 12 75.41 2.78 1.2605 4 0 4 12 75.99 1.50 1.2523 4 0 5 12 76.79 2.86 1.2413 1 1 24 12 78.52 1.98 1.2182 4 0 8 12 79.46 1.04 1.2061 2 0 24 12 79.61 1.31 1.2042 4 0 9 12 82.16 1.39 1.1732 0 0 28 2 83.20 4.76 1.1612 1 1 26 12 86.79 1.17 1.1221 3 0 22 12 87.63 1.04 1.1135 4 1 0 12 88.40 1.17 1.1058 1 0 29 12 88.71 1.58 1.1027 3 2 10 24 88.75 3.12 1.1023 4 0 15 12 89.34 7.54 1.0966 2 2 20 12 89.91 2.88 1.0911 4 1 6 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.