Barioferrite Collomb A, Wolfers P, Obradors X Journal of Magnetism and Magnetic Materials 62 (1986) 57-67 Neutron diffraction studies of some hexagonal ferrites: BaFe12O19, BaMg2-W and CaCo2-W Note: T = 4.2 K Sample: BaCo2 - W Locality: synthetic _database_code_amcsd 0013061 CELL PARAMETERS: 5.8990 5.8990 32.8460 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 989.851 Density (g/cm3): 5.302 MAX. ABS. INTENSITY / VOLUME**2: 37.85686924 RIR: 2.325 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.19 1.03 5.4743 0 0 6 2 18.19 11.68 4.8781 1 0 2 12 19.17 5.81 4.6295 1 0 3 12 21.64 6.48 4.1058 0 0 8 2 23.82 1.08 3.7350 1 0 6 12 27.15 6.52 3.2846 0 0 10 2 30.09 20.31 2.9696 1 0 9 12 30.30 46.03 2.9495 1 1 0 6 30.80 2.75 2.9031 1 1 2 12 32.25 9.46 2.7759 1 1 4 12 32.40 61.27 2.7628 1 0 10 12 32.72 10.69 2.7372 0 0 12 2 34.54 100.00 2.5966 1 1 6 12 34.80 35.24 2.5779 1 0 11 12 35.13 1.16 2.5543 2 0 0 6 35.24 14.26 2.5467 2 0 1 12 35.57 8.44 2.5240 2 0 2 12 36.11 6.97 2.4875 2 0 3 12 36.85 32.31 2.4391 2 0 4 12 37.55 8.14 2.3955 1 1 8 12 37.79 11.00 2.3807 2 0 5 12 38.91 7.76 2.3148 2 0 6 12 40.20 2.22 2.2435 2 0 7 12 41.64 27.80 2.1689 2 0 8 12 42.40 3.48 2.1321 1 0 14 12 43.23 11.23 2.0927 2 0 9 12 44.96 1.62 2.0164 2 0 10 12 46.80 1.03 1.9410 2 0 11 12 47.41 1.09 1.9177 2 1 2 24 47.75 2.12 1.9048 1 0 16 12 48.76 1.50 1.8675 2 0 12 12 49.65 1.26 1.8361 1 1 14 12 50.50 1.73 1.8072 1 0 17 12 50.83 1.88 1.7963 2 0 13 12 53.00 1.92 1.7279 2 0 14 12 53.70 7.13 1.7067 2 1 9 24 53.84 7.56 1.7029 3 0 0 6 54.46 2.29 1.6849 1 1 16 12 55.08 1.74 1.6674 3 0 4 12 55.18 21.63 1.6646 2 1 10 24 55.25 16.24 1.6625 2 0 15 12 55.99 5.99 1.6423 0 0 20 2 56.60 20.44 1.6260 3 0 6 12 56.78 16.93 1.6214 2 1 11 24 57.60 23.06 1.6001 2 0 16 12 58.69 1.89 1.5730 3 0 8 12 59.09 1.26 1.5635 1 0 20 12 59.58 1.88 1.5518 1 1 18 12 60.04 7.45 1.5409 2 0 17 12 62.27 2.99 1.4909 2 1 14 24 62.56 6.57 1.4848 2 0 18 12 63.03 47.30 1.4748 2 2 0 6 65.16 9.06 1.4317 2 0 19 12 66.48 1.39 1.4065 2 1 16 24 67.48 1.11 1.3879 2 2 8 12 67.84 2.64 1.3814 2 0 20 12 68.73 1.53 1.3658 2 1 17 24 69.92 1.82 1.3454 2 2 10 12 70.61 2.00 1.3339 2 0 21 12 70.72 2.01 1.3321 1 1 22 12 71.42 2.26 1.3208 3 1 9 24 72.68 8.53 1.3010 3 1 10 24 72.85 4.72 1.2983 2 2 12 12 74.06 5.46 1.2801 3 1 11 24 74.32 1.33 1.2762 4 0 1 12 74.58 1.98 1.2724 1 0 25 12 75.31 3.20 1.2620 4 0 4 12 75.89 1.42 1.2537 4 0 5 12 76.78 2.11 1.2415 1 1 24 12 78.42 2.38 1.2195 4 0 8 12 79.44 1.30 1.2063 2 0 24 12 82.17 1.08 1.1731 0 0 28 2 83.19 4.63 1.1613 1 1 26 12 86.74 1.01 1.1226 3 0 22 12 88.60 1.59 1.1038 3 2 10 24 88.66 3.02 1.1032 4 0 15 12 89.27 7.48 1.0973 2 2 20 12 89.78 2.88 1.0924 4 1 6 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.