Barioferrite Collomb A, Wolfers P, Obradors X Journal of Magnetism and Magnetic Materials 62 (1986) 57-67 Neutron diffraction studies of some hexagonal ferrites: BaFe12O19, BaMg2-W and BaCo2-W Locality: synthetic _cod_database_code 1008327 _database_code_amcsd 0016241 CELL PARAMETERS: 5.9281 5.9281 23.4070 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 712.373 Density (g/cm3): 5.181 MAX. ABS. INTENSITY / VOLUME**2: 42.27654155 RIR: 2.657 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.69 6.03 5.0147 1 0 1 12 18.88 11.31 4.7014 1 0 2 12 22.79 9.98 3.9012 0 0 6 2 23.05 2.94 3.8592 1 0 4 12 28.74 1.20 3.1061 1 0 6 12 30.15 44.94 2.9641 1 1 0 6 30.55 15.16 2.9259 0 0 8 2 31.13 8.36 2.8733 1 1 2 12 31.94 89.18 2.8019 1 0 7 12 33.90 100.00 2.6442 1 1 4 12 34.95 9.47 2.5669 2 0 0 6 35.17 6.52 2.5516 2 0 1 12 35.31 7.56 2.5420 1 0 8 12 35.81 1.21 2.5073 2 0 2 12 36.86 47.02 2.4384 2 0 3 12 38.13 3.31 2.3601 1 1 6 12 38.81 1.75 2.3201 1 0 9 12 40.06 26.31 2.2508 2 0 5 12 42.14 17.43 2.1444 2 0 6 12 42.44 1.50 2.1298 1 0 10 12 46.18 5.41 1.9657 1 0 11 12 49.63 2.26 1.8370 1 1 10 12 49.92 7.27 1.8269 2 0 9 12 52.94 3.20 1.7296 2 0 10 12 53.55 7.37 1.7113 3 0 0 6 54.17 1.51 1.6933 3 0 2 12 54.69 35.49 1.6783 2 1 7 24 54.92 5.73 1.6719 0 0 14 2 55.99 19.81 1.6425 3 0 4 12 56.14 41.22 1.6382 2 0 11 12 56.47 2.89 1.6294 1 1 12 12 56.94 4.99 1.6171 2 1 8 24 59.52 2.45 1.5531 2 0 12 12 62.14 1.07 1.4939 2 1 10 24 62.18 1.54 1.4930 1 0 15 12 62.69 40.63 1.4820 2 2 0 6 63.07 2.95 1.4741 2 0 13 12 65.05 3.42 1.4338 2 1 11 24 66.77 11.12 1.4010 2 0 14 12 67.62 1.95 1.3854 2 2 6 12 71.34 5.73 1.3221 2 2 8 12 71.98 2.19 1.3119 1 1 16 12 72.10 12.27 1.3101 3 1 7 24 73.64 1.12 1.2864 3 0 12 12 74.05 1.26 1.2803 3 1 8 24 74.99 4.48 1.2665 4 0 3 12 75.40 2.67 1.2606 1 0 18 12 77.04 2.01 1.2378 4 0 5 12 78.44 1.48 1.2192 4 0 6 12 78.69 1.34 1.2160 2 1 15 24 78.89 1.54 1.2134 2 0 17 12 80.69 4.79 1.1908 1 1 18 12 81.30 1.61 1.1834 3 1 11 24 82.40 1.30 1.1703 0 0 20 2 84.10 1.02 1.1510 4 0 9 12 87.78 1.13 1.1120 3 0 16 12 87.89 2.03 1.1109 3 2 7 24 88.07 6.82 1.1090 2 2 14 12 88.96 2.79 1.1003 4 1 4 24 89.09 8.01 1.0990 4 0 11 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.