Ba0.99 Fe6.02 O11 Zn0.94 Muller J, Collomb A, Fournier T, Harrowfield I, Samaras D Journal of Magnetism and Magnetic Materials 102 (1991) 305-313 Composition and structure of some (Ba1-pSrp)Zn Fe6O11Y-type hexagonal ferrites _cod_database_code 1008505 _database_code_amcsd 0016398 CELL PARAMETERS: 5.8723 5.8723 43.5560 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1300.754 Density (g/cm3): 5.435 MAX. ABS. INTENSITY / VOLUME**2: 36.12934208 RIR: 2.165 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.56 3.92 5.0512 1 0 1 6 17.91 1.77 4.9523 0 1 2 6 19.26 8.79 4.6078 1 0 4 6 20.22 2.58 4.3919 0 1 5 6 22.58 3.93 3.9377 1 0 7 6 23.94 5.91 3.7165 0 1 8 6 24.53 12.45 3.6297 0 0 12 2 26.95 1.24 3.3081 1 0 10 6 28.57 3.70 3.1243 0 1 11 6 30.44 100.00 2.9362 1 1 0 6 30.79 18.20 2.9037 0 0 15 2 31.08 27.38 2.8779 1 1 3 12 31.99 81.40 2.7978 1 0 13 6 32.91 30.68 2.7219 1 1 6 12 33.77 49.45 2.6539 0 1 14 6 35.36 6.60 2.5385 0 2 1 6 35.55 1.40 2.5256 2 0 2 6 35.77 79.09 2.5103 1 1 9 12 36.28 24.38 2.4762 0 2 4 6 36.82 26.97 2.4409 2 0 5 6 37.47 10.38 2.4000 1 0 16 6 38.24 10.12 2.3538 0 2 7 6 39.48 1.00 2.2828 1 1 12 12 41.10 61.63 2.1960 0 2 10 6 43.85 3.70 2.0646 1 1 15 12 45.30 5.48 2.0020 0 1 20 6 48.77 1.66 1.8673 1 1 18 12 49.02 11.21 1.8582 0 2 16 6 49.40 2.72 1.8449 1 0 22 6 49.64 1.71 1.8365 2 1 7 12 50.34 1.62 1.8125 1 2 8 12 50.57 8.87 1.8048 2 0 17 6 53.84 12.88 1.7026 0 2 19 6 54.10 16.56 1.6952 3 0 0 6 54.50 1.98 1.6837 0 3 3 6 54.50 2.88 1.6837 3 0 3 6 55.08 28.47 1.6673 2 1 13 12 55.56 12.79 1.6541 2 0 20 6 55.68 4.57 1.6508 0 3 6 6 55.68 1.63 1.6508 3 0 6 6 55.77 5.54 1.6482 1 0 25 6 56.26 23.20 1.6352 1 2 14 12 57.09 6.04 1.6132 0 0 27 2 57.61 8.87 1.5999 0 3 9 6 57.61 8.02 1.5999 3 0 9 6 57.96 1.84 1.5911 0 1 26 6 58.81 7.09 1.5702 2 1 16 12 59.14 13.69 1.5621 0 2 22 6 59.92 3.36 1.5437 1 1 24 12 61.01 10.03 1.5188 2 0 23 6 62.43 1.44 1.4875 1 0 28 6 63.35 50.38 1.4681 2 2 0 6 64.68 4.60 1.4411 1 2 20 12 64.88 5.60 1.4372 0 2 25 6 66.09 2.99 1.4138 1 1 27 12 66.88 12.00 1.3989 2 0 26 6 67.97 1.22 1.3791 2 1 22 12 69.01 2.69 1.3610 2 2 12 12 71.79 2.06 1.3148 0 1 32 6 72.09 6.74 1.3101 2 2 15 12 72.65 4.08 1.3015 1 1 30 12 72.74 10.92 1.3000 1 3 13 12 73.34 3.60 1.2909 2 1 25 12 73.76 7.28 1.2846 3 1 14 12 75.24 1.03 1.2629 1 2 26 12 75.25 2.06 1.2628 4 0 4 6 75.58 2.72 1.2581 0 4 5 6 75.99 2.04 1.2524 1 3 16 12 76.72 1.59 1.2423 1 0 34 6 78.35 5.30 1.2205 4 0 10 6 79.22 1.45 1.2092 2 1 28 12 79.25 1.14 1.2088 0 1 35 6 79.64 3.14 1.2038 1 1 33 12 81.26 1.62 1.1839 3 1 20 12 84.02 1.49 1.1519 4 0 16 6 85.21 1.31 1.1389 0 4 17 6 87.13 1.34 1.1186 1 1 36 12 87.79 2.20 1.1118 4 0 19 6 87.90 1.61 1.1108 1 2 32 12 88.00 2.19 1.1098 4 1 0 12 88.71 1.45 1.1027 3 0 30 6 88.80 2.06 1.1018 3 2 13 12 89.20 2.33 1.0980 0 4 20 6 89.37 2.25 1.0963 1 3 25 12 89.77 1.14 1.0924 2 3 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.