Ba0.7 Fe6.16 O11 Sr0.27 Zn0.83 Muller J, Collomb A, Fournier T, Harrowfield I, Samaras D Journal of Magnetism and Magnetic Materials 102 (1991) 305-313 Composition and structure of some (Ba1-pSrp)Zn Fe6O11Y-type hexagonal ferrites _cod_database_code 1008506 _database_code_amcsd 0016399 CELL PARAMETERS: 5.8656 5.8656 43.5030 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1296.208 Density (g/cm3): 5.334 MAX. ABS. INTENSITY / VOLUME**2: 33.05931972 RIR: 2.018 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 6.09 2.95 14.5010 0 0 3 2 17.58 2.81 5.0455 1 0 1 6 19.29 8.24 4.6025 1 0 4 6 22.61 2.61 3.9331 1 0 7 6 23.97 3.85 3.7121 0 1 8 6 24.56 11.64 3.6252 0 0 12 2 28.61 3.11 3.1206 0 1 11 6 30.48 100.00 2.9328 1 1 0 6 30.83 17.70 2.9002 0 0 15 2 31.11 23.62 2.8746 1 1 3 12 32.03 80.53 2.7945 1 0 13 6 32.94 31.76 2.7188 1 1 6 12 33.82 54.57 2.6507 0 1 14 6 35.40 8.15 2.5356 0 2 1 6 35.81 85.32 2.5074 1 1 9 12 36.32 27.64 2.4733 0 2 4 6 36.87 25.75 2.4381 2 0 5 6 37.52 9.89 2.3972 1 0 16 6 38.28 9.45 2.3511 0 2 7 6 41.15 62.21 2.1934 0 2 10 6 43.90 2.72 2.0622 1 1 15 12 45.36 4.91 1.9995 0 1 20 6 48.83 1.05 1.8651 1 1 18 12 49.08 10.75 1.8560 0 2 16 6 49.46 2.42 1.8427 1 0 22 6 49.70 1.34 1.8344 2 1 7 12 50.41 1.14 1.8104 1 2 8 12 50.64 9.02 1.8027 2 0 17 6 53.91 14.43 1.7006 0 2 19 6 54.17 16.54 1.6933 3 0 0 6 54.57 1.68 1.6818 0 3 3 6 54.57 2.52 1.6818 3 0 3 6 55.15 28.12 1.6653 2 1 13 12 55.63 13.21 1.6521 2 0 20 6 55.75 4.75 1.6489 0 3 6 6 55.75 1.67 1.6489 3 0 6 6 55.85 5.00 1.6462 1 0 25 6 56.33 25.52 1.6333 1 2 14 12 57.17 6.44 1.6112 0 0 27 2 57.69 9.54 1.5980 0 3 9 6 57.69 8.64 1.5980 3 0 9 6 58.04 1.58 1.5892 0 1 26 6 58.88 6.88 1.5684 2 1 16 12 59.22 13.91 1.5603 0 2 22 6 60.00 3.73 1.5419 1 1 24 12 61.09 12.51 1.5170 2 0 23 6 62.51 1.21 1.4857 1 0 28 6 63.43 53.04 1.4664 2 2 0 6 64.77 4.21 1.4394 1 2 20 12 64.96 5.40 1.4355 0 2 25 6 66.18 2.97 1.4121 1 1 27 12 66.97 11.90 1.3973 2 0 26 6 68.06 1.06 1.3775 2 1 22 12 69.10 2.48 1.3594 2 2 12 12 71.89 2.49 1.3133 0 1 32 6 72.19 6.56 1.3086 2 2 15 12 72.75 3.81 1.2999 1 1 30 12 72.84 10.79 1.2985 1 3 13 12 73.44 3.17 1.2894 2 1 25 12 73.86 8.03 1.2831 3 1 14 12 75.35 2.33 1.2614 4 0 4 6 75.68 2.62 1.2566 0 4 5 6 76.09 1.93 1.2509 1 3 16 12 76.83 1.78 1.2407 1 0 34 6 78.45 5.28 1.2191 4 0 10 6 79.33 1.25 1.2078 2 1 28 12 79.76 3.04 1.2024 1 1 33 12 81.38 1.46 1.1825 3 1 20 12 84.13 1.43 1.1506 4 0 16 6 85.33 1.32 1.1376 0 4 17 6 87.26 1.74 1.1173 1 1 36 12 87.92 2.47 1.1106 4 0 19 6 88.03 1.99 1.1095 1 2 32 12 88.13 2.19 1.1085 4 1 0 12 88.84 1.37 1.1014 3 0 30 6 88.93 2.04 1.1005 3 2 13 12 89.33 2.40 1.0967 0 4 20 6 89.51 2.03 1.0950 1 3 25 12 89.90 1.26 1.0912 2 3 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.