Ba0.49 Fe6.13 O11 Sr0.47 Zn0.84 Muller J, Collomb A, Fournier T, Harrowfield I, Samaras D Journal of Magnetism and Magnetic Materials 102 (1991) 305-313 Composition and structure of some (Ba1-pSrp)Zn Fe6O11Y-type hexagonal ferrites _cod_database_code 1008507 _database_code_amcsd 0016400 CELL PARAMETERS: 5.8629 5.8629 43.4640 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1293.854 Density (g/cm3): 5.249 MAX. ABS. INTENSITY / VOLUME**2: 30.70225676 RIR: 1.905 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 6.10 7.68 14.4880 0 0 3 2 12.22 1.18 7.2440 0 0 6 2 17.59 2.26 5.0431 1 0 1 6 19.30 8.76 4.6000 1 0 4 6 22.62 1.71 3.9306 1 0 7 6 23.99 2.59 3.7096 0 1 8 6 24.58 11.23 3.6220 0 0 12 2 28.63 2.54 3.1183 0 1 11 6 30.49 100.00 2.9314 1 1 0 6 30.86 17.57 2.8976 0 0 15 2 31.13 21.60 2.8732 1 1 3 12 32.05 78.89 2.7924 1 0 13 6 32.96 32.12 2.7174 1 1 6 12 33.84 59.61 2.6487 0 1 14 6 35.42 9.43 2.5344 0 2 1 6 35.83 90.59 2.5059 1 1 9 12 36.34 30.03 2.4721 0 2 4 6 36.88 25.19 2.4369 2 0 5 6 37.55 9.47 2.3952 1 0 16 6 38.30 8.88 2.3499 0 2 7 6 41.18 63.35 2.1922 0 2 10 6 43.94 2.07 2.0608 1 1 15 12 45.40 4.43 1.9979 0 1 20 6 49.12 10.44 1.8548 0 2 16 6 49.51 2.27 1.8412 1 0 22 6 49.73 1.05 1.8335 2 1 7 12 50.67 9.37 1.8015 2 0 17 6 53.95 15.68 1.6994 0 2 19 6 54.19 16.53 1.6925 3 0 0 6 54.59 1.52 1.6810 0 3 3 6 54.59 2.33 1.6810 3 0 3 6 55.19 27.56 1.6644 2 1 13 12 55.67 13.53 1.6509 2 0 20 6 55.78 4.88 1.6481 0 3 6 6 55.78 1.65 1.6481 3 0 6 6 55.90 4.58 1.6448 1 0 25 6 56.36 28.01 1.6324 1 2 14 12 57.23 6.77 1.6098 0 0 27 2 57.72 10.15 1.5972 0 3 9 6 57.72 9.15 1.5972 3 0 9 6 58.09 1.25 1.5878 0 1 26 6 58.92 6.74 1.5674 2 1 16 12 59.27 14.08 1.5592 0 2 22 6 60.05 4.31 1.5407 1 1 24 12 61.14 14.75 1.5159 2 0 23 6 62.57 1.02 1.4845 1 0 28 6 63.47 55.38 1.4657 2 2 0 6 64.81 3.91 1.4385 1 2 20 12 65.02 5.32 1.4344 0 2 25 6 66.23 2.96 1.4110 1 1 27 12 67.03 11.55 1.3962 2 0 26 6 69.14 2.37 1.3587 2 2 12 12 71.97 2.80 1.3121 0 1 32 6 72.23 6.53 1.3079 2 2 15 12 72.82 3.71 1.2988 1 1 30 12 72.89 10.57 1.2978 1 3 13 12 73.50 2.87 1.2885 2 1 25 12 73.90 8.77 1.2825 3 1 14 12 75.39 2.53 1.2608 4 0 4 6 75.73 2.58 1.2560 0 4 5 6 76.14 1.86 1.2502 1 3 16 12 76.91 2.02 1.2397 1 0 34 6 77.14 1.01 1.2365 3 0 24 6 78.50 5.33 1.2185 4 0 10 6 79.40 1.07 1.2069 2 1 28 12 79.84 2.90 1.2014 1 1 33 12 81.43 1.34 1.1818 3 1 20 12 84.19 1.37 1.1500 4 0 16 6 85.39 1.37 1.1369 0 4 17 6 87.35 2.17 1.1164 1 1 36 12 87.99 2.69 1.1099 4 0 19 6 88.11 2.25 1.1087 1 2 32 12 88.18 2.19 1.1080 4 1 0 12 88.92 1.35 1.1006 3 0 30 6 88.99 2.00 1.1000 3 2 13 12 89.39 2.45 1.0961 0 4 20 6 89.58 1.85 1.0943 1 3 25 12 89.96 1.37 1.0906 2 3 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.