Ba0.28 Fe6.07 O11 Sr0.67 Zn0.88 Muller J, Collomb A, Fournier T, Harrowfield I, Samaras D Journal of Magnetism and Magnetic Materials 102 (1991) 305-313 Composition and structure of some (Ba1-pSrp)Zn Fe6O11Y-type hexagonal ferrites _cod_database_code 1008508 _database_code_amcsd 0016401 CELL PARAMETERS: 5.8585 5.8585 43.4120 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1290.367 Density (g/cm3): 5.170 MAX. ABS. INTENSITY / VOLUME**2: 28.81809376 RIR: 1.815 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 6.11 14.37 14.4707 0 0 3 2 12.23 2.33 7.2353 0 0 6 2 17.60 1.82 5.0393 1 0 1 6 19.31 9.25 4.5962 1 0 4 6 24.01 1.42 3.7061 0 1 8 6 24.61 10.93 3.6177 0 0 12 2 28.66 1.78 3.1151 0 1 11 6 30.52 100.00 2.9293 1 1 0 6 30.90 16.97 2.8941 0 0 15 2 31.15 19.79 2.8710 1 1 3 12 32.09 76.30 2.7894 1 0 13 6 32.99 31.95 2.7152 1 1 6 12 33.88 65.05 2.6458 0 1 14 6 35.45 10.72 2.5325 0 2 1 6 35.87 97.18 2.5037 1 1 9 12 36.37 32.70 2.4702 0 2 4 6 36.91 24.01 2.4350 2 0 5 6 37.59 8.87 2.3926 1 0 16 6 38.34 8.20 2.3480 0 2 7 6 41.22 65.06 2.1903 0 2 10 6 43.98 1.54 2.0588 1 1 15 12 45.45 3.87 1.9956 0 1 20 6 46.24 1.15 1.9635 2 0 14 6 49.17 9.76 1.8530 0 2 16 6 49.57 2.15 1.8391 1 0 22 6 50.73 9.89 1.7997 2 0 17 6 51.67 1.03 1.7690 0 1 23 6 54.01 16.67 1.6977 0 2 19 6 54.24 16.78 1.6912 3 0 0 6 54.31 1.03 1.6890 1 1 21 12 54.64 1.43 1.6798 0 3 3 6 54.64 2.19 1.6798 3 0 3 6 55.24 27.09 1.6630 2 1 13 12 55.74 13.83 1.6493 2 0 20 6 55.83 5.04 1.6468 0 3 6 6 55.83 1.61 1.6468 3 0 6 6 55.97 4.23 1.6429 1 0 25 6 56.42 31.28 1.6310 1 2 14 12 57.30 7.29 1.6079 0 0 27 2 57.77 11.07 1.5960 0 3 9 6 57.77 9.88 1.5960 3 0 9 6 58.98 6.55 1.5660 2 1 16 12 59.33 14.46 1.5575 0 2 22 6 60.12 5.22 1.5390 1 1 24 12 61.21 18.12 1.5143 2 0 23 6 63.52 58.73 1.4646 2 2 0 6 64.88 3.65 1.4371 1 2 20 12 65.10 5.19 1.4329 0 2 25 6 66.32 3.12 1.4095 1 1 27 12 67.11 11.09 1.3947 2 0 26 6 69.20 2.33 1.3576 2 2 12 12 72.06 3.10 1.3106 0 1 32 6 72.30 6.48 1.3068 2 2 15 12 72.91 3.63 1.2974 1 1 30 12 72.95 10.52 1.2967 1 3 13 12 73.59 2.69 1.2872 2 1 25 12 73.97 9.85 1.2814 3 1 14 12 74.90 1.09 1.2679 4 0 1 6 75.46 2.82 1.2598 4 0 4 6 75.79 2.52 1.2551 0 4 5 6 76.22 1.79 1.2492 1 3 16 12 77.01 2.37 1.2382 1 0 34 6 77.22 1.25 1.2354 3 0 24 6 78.57 5.60 1.2175 4 0 10 6 79.94 2.68 1.2001 1 1 33 12 81.52 1.29 1.1808 3 1 20 12 84.28 1.28 1.1490 4 0 16 6 85.47 1.49 1.1360 0 4 17 6 87.47 2.80 1.1151 1 1 36 12 88.08 2.90 1.1090 4 0 19 6 88.23 2.46 1.1075 1 2 32 12 88.26 2.31 1.1072 4 1 0 12 89.04 1.37 1.0995 3 0 30 6 89.08 2.03 1.0991 3 2 13 12 89.49 2.57 1.0951 0 4 20 6 89.68 1.79 1.0933 1 3 25 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.