Fe6 Ge6 Tb Zaharko O, Schobinger-Papamantellos P, Ritter C, Rodriguez-Carvajal J, Buschow K Journal of Magnetism and Magnetic Materials 187 (1998) 293-308 Influence of thermal history on crystal structure, microstructure and magnetic properties of Tb Fe6 Ge6 (II) _cod_database_code 1006166 _database_code_amcsd 0013067 CELL PARAMETERS: 8.1307 17.6990 5.1262 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 737.685 Density (g/cm3): 8.371 MAX. ABS. INTENSITY / VOLUME**2: 81.73058138 RIR: 3.179 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.98 7.87 7.3884 1 1 0 4 18.58 2.72 4.7751 1 3 0 4 20.02 1.49 4.4357 0 2 1 4 21.09 5.19 4.2117 1 1 1 8 21.86 1.05 4.0654 2 0 0 2 25.49 4.06 3.4940 1 3 1 8 27.48 1.47 3.2456 1 5 0 4 29.81 5.00 2.9970 2 2 1 8 29.85 2.45 2.9936 2 4 0 4 32.66 3.29 2.7422 1 5 1 8 33.45 15.36 2.6790 3 1 0 4 35.01 36.94 2.5631 0 0 2 2 35.10 72.81 2.5567 0 6 1 4 36.48 11.58 2.4628 3 3 0 4 37.89 21.91 2.3743 3 1 1 8 40.64 18.86 2.2199 3 3 1 8 40.68 50.84 2.2179 0 4 2 4 40.79 25.49 2.2124 0 8 0 2 41.66 50.64 2.1681 2 0 2 4 41.73 100.00 2.1643 2 6 1 8 41.99 8.34 2.1519 3 5 0 4 44.58 35.73 2.0327 4 0 0 2 45.73 14.53 1.9842 3 5 1 8 46.65 41.74 1.9470 2 4 2 8 46.75 20.45 1.9433 2 8 0 4 49.20 9.48 1.8520 3 1 2 8 49.29 4.83 1.8488 3 7 0 4 49.31 11.95 1.8479 4 2 1 8 49.34 6.00 1.8471 4 4 0 4 51.46 8.02 1.7759 3 3 2 8 52.63 6.06 1.7392 3 7 1 8 55.78 6.69 1.6481 3 5 2 8 57.90 3.21 1.5926 4 0 2 4 57.94 3.31 1.5917 3 9 0 4 57.96 6.29 1.5911 4 6 1 8 59.90 1.09 1.5441 5 1 1 8 60.95 3.85 1.5201 3 9 1 8 61.88 4.41 1.4994 3 7 2 8 61.89 1.09 1.4991 5 3 1 8 61.92 4.74 1.4985 4 4 2 8 62.00 2.42 1.4968 4 8 0 4 62.85 11.86 1.4786 0 6 3 4 63.03 5.74 1.4749 0 12 0 2 64.70 3.82 1.4406 3 1 3 8 65.77 1.10 1.4199 5 5 1 8 66.61 3.67 1.4039 3 3 3 8 67.39 20.17 1.3895 2 6 3 8 67.56 9.78 1.3865 2 12 0 4 67.73 2.29 1.3836 3 11 0 4 69.35 1.10 1.3551 6 0 0 2 69.52 3.49 1.3522 3 9 2 8 70.35 3.37 1.3382 3 5 3 8 70.50 3.10 1.3358 3 11 1 8 73.00 3.23 1.2960 6 2 1 8 73.02 1.60 1.2957 6 4 0 4 73.14 3.31 1.2939 4 2 3 8 73.23 3.24 1.2926 4 8 2 8 73.28 3.27 1.2917 4 10 1 8 73.96 12.40 1.2815 0 0 4 2 74.18 24.18 1.2784 0 12 2 4 75.81 1.71 1.2549 3 7 3 8 78.57 2.79 1.2175 3 11 2 8 80.11 10.53 1.1980 6 0 2 4 80.16 20.89 1.1973 6 6 1 8 80.29 2.12 1.1957 4 6 3 8 80.45 1.00 1.1938 4 12 0 4 81.28 1.76 1.1837 3 13 1 8 82.89 1.35 1.1647 3 9 3 8 83.62 1.65 1.1564 6 4 2 8 83.65 1.59 1.1561 3 1 4 8 85.39 1.44 1.1368 3 3 4 8 88.08 3.70 1.1089 0 8 4 4 88.36 1.85 1.1062 0 16 0 2 88.88 1.43 1.1011 3 5 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.