Strontium Hirst R G, King A J, Kanda F A Journal of Physical Chemistry 60 (1956) 302-304 The barium-strontium equilibrium system Locality: synthetic Sample: at T = 225 C note: known as gamma-strontium _database_code_amcsd 0013144 CELL PARAMETERS: 4.2800 4.2800 7.0500 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 111.843 Density (g/cm3): 2.601 MAX. ABS. INTENSITY / VOLUME**2: 92.03025210 RIR: 11.519 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 24.01 23.05 3.7066 1 0 0 6 25.27 26.94 3.5250 0 0 2 2 27.18 100.00 3.2808 1 0 1 12 35.13 16.27 2.5543 1 0 2 12 42.23 18.47 2.1400 1 1 0 6 45.71 21.37 1.9847 1 0 3 12 49.16 2.78 1.8533 2 0 0 6 49.85 21.23 1.8293 1 1 2 12 50.95 14.76 1.7924 2 0 1 12 51.88 3.08 1.7625 0 0 4 2 56.06 3.50 1.6404 2 0 2 12 57.94 3.11 1.5917 1 0 4 12 63.98 6.49 1.4552 2 0 3 12 66.77 1.85 1.4010 2 1 0 12 68.26 10.24 1.3741 2 1 1 24 69.03 6.55 1.3605 1 1 4 12 71.60 4.30 1.3179 1 0 5 12 72.62 2.73 1.3019 2 1 2 24 74.26 1.26 1.2772 2 0 4 12 77.21 2.20 1.2355 3 0 0 6 79.68 5.94 1.2034 2 1 3 24 82.78 3.50 1.1660 3 0 2 12 86.79 2.28 1.1222 2 0 5 12 89.33 1.40 1.0967 2 1 4 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.