Calcium Schottmiller J C, King A J, Kanda F A Journal of Physical Chemistry 62 (1958) 1446-1449 The calcium-strontium metal phase system Locality: synthetic Sample: at T = 415 C _database_code_amcsd 0013146 CELL PARAMETERS: 4.0000 4.0000 6.5000 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 90.067 Density (g/cm3): 1.478 MAX. ABS. INTENSITY / VOLUME**2: 27.83961449 RIR: 6.135 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 25.72 23.85 3.4641 1 0 0 6 27.44 26.54 3.2500 0 0 2 2 29.21 100.00 3.0571 1 0 1 12 37.96 15.05 2.3702 1 0 2 12 45.34 16.54 2.0000 1 1 0 6 49.63 17.93 1.8369 1 0 3 12 52.86 2.36 1.7321 2 0 0 6 53.82 17.65 1.7033 1 1 2 12 54.85 12.31 1.6737 2 0 1 12 56.64 2.42 1.6250 0 0 4 2 60.58 2.79 1.5285 2 0 2 12 63.20 2.36 1.4712 1 0 4 12 69.48 4.89 1.3529 2 0 3 12 72.14 1.41 1.3093 2 1 0 12 73.83 7.75 1.2835 2 1 1 24 75.36 4.79 1.2612 1 1 4 12 78.60 3.08 1.2171 1 0 5 12 78.81 2.04 1.2145 2 1 2 24 83.77 1.66 1.1547 3 0 0 6 86.94 4.43 1.1206 2 1 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.