BaTiO3 Kwei G H, Lawson A C, Billinge S J L, Cheong S W Journal of Physical Chemistry 97 (1993) 2368-2377 Structures of the ferroelectric phases of barium titanate Locality: synthetic Note: T = 15 K _database_code_amcsd 0018583 CELL PARAMETERS: 4.0036 4.0036 4.0036 89.839 89.839 89.839 SPACE GROUP: R3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 64.172 Density (g/cm3): 6.033 MAX. ABS. INTENSITY / VOLUME**2: 106.0970645 RIR: 5.726 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.20 37.44 4.0036 1 0 0 3 31.56 100.00 2.8349 1 1 0 3 31.65 98.90 2.8270 0 -1 1 6 38.85 12.34 2.3180 1 1 1 1 39.00 35.53 2.3093 1 -1 1 3 45.30 65.36 2.0018 2 0 0 3 50.95 7.61 1.7925 2 1 0 6 51.07 7.09 1.7884 0 -1 2 6 56.14 16.20 1.6383 2 1 1 3 56.31 32.16 1.6337 2 -1 1 6 56.37 16.13 1.6322 1 -2 1 3 65.90 16.37 1.4175 2 2 0 3 66.10 16.93 1.4135 0 -2 2 6 70.37 1.38 1.3379 2 2 1 3 70.57 1.18 1.3345 3 0 0 3 70.57 1.21 1.3345 2 -1 2 3 70.68 2.24 1.3329 2 -2 1 6 74.95 12.00 1.2671 3 1 0 6 75.10 11.89 1.2650 0 -1 3 6 79.21 2.88 1.2093 3 1 1 3 79.41 5.37 1.2068 3 -1 1 6 79.50 2.58 1.2056 -1 -1 3 3 83.39 2.28 1.1590 2 2 2 1 83.77 7.40 1.1547 2 -2 2 3 87.80 1.27 1.1118 3 2 0 6 88.08 1.04 1.1090 0 -2 3 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.