BaTiO3 Kwei G H, Lawson A C, Billinge S J L, Cheong S W Journal of Physical Chemistry 97 (1993) 2368-2377 Structures of the ferroelectric phases of barium titanate Locality: synthetic Note: T = 130 K _database_code_amcsd 0018588 CELL PARAMETERS: 4.0038 4.0038 4.0038 89.843 89.843 89.843 SPACE GROUP: R3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 64.184 Density (g/cm3): 6.032 MAX. ABS. INTENSITY / VOLUME**2: 106.0066909 RIR: 5.722 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.20 37.54 4.0038 1 0 0 3 31.56 100.00 2.8350 1 1 0 3 31.65 99.17 2.8273 0 -1 1 6 38.85 12.45 2.3179 1 1 1 1 39.00 35.44 2.3095 1 -1 1 3 45.30 65.40 2.0019 2 0 0 3 50.94 7.72 1.7925 2 1 0 6 51.06 7.07 1.7886 0 -1 2 6 56.14 16.12 1.6383 2 1 1 3 56.31 32.26 1.6338 2 -1 1 6 56.37 16.22 1.6323 1 -2 1 3 65.89 16.37 1.4175 2 2 0 3 66.10 16.96 1.4136 0 -2 2 6 70.37 1.43 1.3379 2 2 1 3 70.57 1.20 1.3346 3 0 0 3 70.57 1.22 1.3346 2 -1 2 3 70.67 2.22 1.3330 2 -2 1 6 74.95 12.00 1.2672 3 1 0 6 75.09 11.98 1.2651 0 -1 3 6 79.21 2.94 1.2093 3 1 1 3 79.40 5.36 1.2069 3 -1 1 6 79.49 2.54 1.2057 -1 -1 3 3 83.39 2.28 1.1590 2 2 2 1 83.77 7.41 1.1548 2 -2 2 3 87.79 1.33 1.1119 3 2 0 6 88.07 1.03 1.1091 0 -2 3 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.