(Li.5K.5)2CO3 Idemoto Y, Richardson J W, Koura N, Kohara S, Loong C K Journal of Physics and Chemistry of Solids 59 (1998) 363-376 Crystal structure of (LixK1-x)2CO3 (x = 0,0.43,0.5,0.62,1) by neutron powder diffraction analysis Sample: contains only 7Li _database_code_amcsd 0013244 CELL PARAMETERS: 7.2228 7.0767 7.5940 90.000 127.421 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 308.273 Density (g/cm3): 2.285 MAX. ABS. INTENSITY / VOLUME**2: 6.261135210 RIR: 0.892 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.34 1.78 4.8381 -1 1 1 4 23.56 2.05 3.7769 -1 0 2 2 25.17 8.43 3.5384 0 2 0 2 26.75 6.89 3.3321 -1 1 2 4 28.04 31.24 3.1820 -2 1 1 4 28.60 16.79 3.1216 -1 2 1 4 29.26 100.00 3.0519 0 2 1 4 29.62 66.42 3.0155 0 0 2 2 29.76 53.87 3.0018 -2 1 2 4 30.04 1.46 2.9751 1 1 1 4 31.18 22.11 2.8682 2 0 0 2 32.27 76.49 2.7742 0 1 2 4 33.72 12.86 2.6581 2 1 0 4 34.74 6.92 2.5822 -1 2 2 4 37.17 1.70 2.4191 -2 2 2 4 37.37 16.70 2.4063 -3 0 2 2 37.39 12.02 2.4050 1 2 1 4 39.53 10.45 2.2798 -1 1 3 4 39.56 27.48 2.2782 -3 1 2 4 40.59 20.89 2.2224 -1 3 1 4 41.09 3.96 2.1969 0 3 1 4 41.39 1.17 2.1816 1 3 0 4 41.44 2.99 2.1790 1 0 2 2 41.95 8.27 2.1537 -3 1 1 4 42.87 9.20 2.1094 -3 1 3 4 43.45 2.51 2.0825 1 1 2 4 44.19 16.56 2.0494 -2 2 3 4 44.31 4.84 2.0443 2 1 1 4 45.56 6.12 1.9908 -1 2 3 4 46.15 22.06 1.9668 -2 3 1 4 46.99 1.56 1.9338 0 1 3 4 47.48 9.85 1.9149 1 3 1 4 47.55 11.92 1.9121 3 0 0 2 47.74 6.33 1.9052 -3 2 1 4 48.19 6.34 1.8885 -2 0 4 2 48.57 1.54 1.8743 -3 2 3 4 49.88 7.62 1.8282 2 2 1 4 49.99 1.51 1.8246 -2 1 4 4 50.07 3.47 1.8219 2 3 0 4 51.00 8.03 1.7908 -3 1 4 4 51.67 2.90 1.7692 0 4 0 2 52.34 5.03 1.7479 0 2 3 4 53.25 1.95 1.7202 -2 3 3 4 54.02 1.83 1.6976 0 4 1 4 54.55 2.85 1.6822 3 2 0 4 55.13 3.62 1.6660 -2 2 4 4 56.07 1.83 1.6402 -3 2 4 4 56.10 3.27 1.6395 2 0 2 2 57.11 1.05 1.6127 -3 3 3 4 57.53 1.28 1.6021 -1 4 2 4 57.72 4.12 1.5972 -4 2 3 4 57.82 2.16 1.5948 -4 1 1 4 58.22 3.23 1.5845 -2 4 1 4 58.28 3.79 1.5831 2 3 1 4 59.13 2.12 1.5625 -1 2 4 4 59.20 2.90 1.5608 -2 4 2 4 59.36 1.65 1.5570 1 4 1 4 60.51 6.37 1.5301 0 3 3 4 62.58 1.23 1.4844 -3 1 5 4 63.04 3.60 1.4747 0 1 4 4 63.28 5.22 1.4695 1 2 3 4 63.93 1.04 1.4562 -3 3 4 4 64.38 1.39 1.4471 -2 1 5 4 64.39 2.69 1.4468 -2 4 3 4 65.04 2.09 1.4340 3 2 1 4 65.39 3.05 1.4272 -4 1 5 4 65.85 2.83 1.4184 -5 0 4 2 68.25 1.83 1.3741 1 5 0 4 68.83 2.35 1.3641 -2 2 5 4 68.90 2.17 1.3628 -5 1 2 4 69.95 2.13 1.3448 -4 3 1 4 70.47 2.88 1.3362 -5 2 3 4 71.68 1.01 1.3166 -5 2 4 4 72.64 2.93 1.3017 -2 5 2 4 72.83 1.66 1.2986 3 4 0 4 73.32 2.41 1.2911 -2 4 4 4 73.98 2.27 1.2812 0 5 2 4 74.10 1.88 1.2795 1 0 4 2 74.34 1.54 1.2760 3 1 2 4 75.56 1.53 1.2583 -5 1 1 4 75.78 1.54 1.2552 -4 4 2 4 76.77 1.54 1.2416 -5 2 5 4 77.53 1.65 1.2313 2 2 3 4 81.63 1.37 1.1795 0 6 0 2 81.83 1.07 1.1771 -1 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.