K2CO3 Idemoto Y, Richardson J W, Koura N, Kohara S, Loong C K Journal of Physics and Chemistry of Solids 59 (1998) 363-376 Crystal structure of (LixK1-x)2CO3 (x = 0,0.43,0.5,0.62,1) by neutron powder diffraction analysis Sample: neutron powder diffraction refinement _database_code_amcsd 0013249 CELL PARAMETERS: 5.6396 9.8391 6.8741 90.000 98.703 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 377.042 Density (g/cm3): 2.434 MAX. ABS. INTENSITY / VOLUME**2: 8.889490219 RIR: 1.189 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.85 3.90 5.5912 0 1 1 4 18.03 1.63 4.9196 0 2 0 2 18.29 2.52 4.8503 1 1 0 4 23.90 1.81 3.7228 1 1 1 4 26.23 30.52 3.3975 0 0 2 2 26.31 1.67 3.3871 -1 2 1 4 28.63 2.44 3.1184 -1 0 2 2 30.06 47.89 2.9727 -1 1 2 4 30.26 3.75 2.9536 0 3 1 4 31.65 100.00 2.8268 1 3 0 4 32.01 60.20 2.7956 0 2 2 4 32.11 52.22 2.7873 2 0 0 2 32.88 8.31 2.7238 1 0 2 2 34.16 66.66 2.6250 1 1 2 4 35.31 1.33 2.5417 1 3 1 4 37.71 28.52 2.3856 -2 2 1 4 37.75 2.97 2.3829 1 2 2 4 37.82 2.55 2.3791 2 1 1 4 38.14 14.15 2.3596 0 3 2 4 38.94 19.15 2.3129 0 4 1 4 40.89 5.67 2.2072 0 1 3 4 41.14 10.39 2.1944 2 2 1 4 41.73 2.06 2.1644 -1 1 3 4 42.87 35.10 2.1095 -2 2 2 4 45.53 21.35 1.9924 0 4 2 4 47.82 2.13 1.9022 -2 3 2 4 48.70 4.56 1.8698 -2 1 3 4 48.93 14.32 1.8614 2 2 2 4 49.10 5.15 1.8556 1 5 0 4 49.42 3.92 1.8443 2 4 0 4 49.61 1.53 1.8377 -1 3 3 4 49.74 2.11 1.8330 -3 1 1 4 49.92 2.23 1.8268 -2 4 1 4 49.95 4.87 1.8259 3 1 0 4 50.32 2.58 1.8134 -1 5 1 4 51.45 6.87 1.7760 -2 2 3 4 51.72 1.87 1.7676 1 5 1 4 52.71 1.91 1.7365 2 4 1 4 53.31 4.27 1.7184 -3 1 2 4 53.45 4.53 1.7143 2 3 2 4 53.90 1.49 1.7011 3 1 1 4 53.98 6.23 1.6987 0 0 4 2 54.16 1.94 1.6935 -2 4 2 4 54.84 4.55 1.6740 0 1 4 4 54.86 1.74 1.6734 -1 1 4 4 55.12 3.24 1.6662 0 4 3 4 55.19 5.19 1.6642 -1 5 2 4 56.08 4.20 1.6399 0 6 0 2 56.77 1.96 1.6217 -3 3 1 4 56.90 2.18 1.6182 2 1 3 4 56.96 7.33 1.6168 3 3 0 4 57.40 1.52 1.6052 -1 2 4 4 57.84 2.06 1.5941 0 6 1 4 59.26 2.30 1.5592 -2 0 4 2 59.36 3.83 1.5568 2 4 2 4 59.66 1.01 1.5498 1 4 3 4 60.08 1.17 1.5400 -2 1 4 4 60.59 1.16 1.5282 3 3 1 4 61.08 1.59 1.5171 3 1 2 4 61.49 3.82 1.5080 -1 3 4 4 66.11 8.81 1.4134 2 6 0 4 66.34 3.92 1.4091 1 3 4 4 66.96 1.09 1.3975 -1 4 4 4 67.17 3.80 1.3937 4 0 0 2 68.95 2.03 1.3619 2 0 4 2 69.70 2.70 1.3490 2 1 4 4 69.87 1.43 1.3462 0 1 5 4 71.55 1.16 1.3187 -1 2 5 4 71.61 2.75 1.3177 1 4 4 4 71.83 3.56 1.3143 -4 2 2 4 72.37 2.70 1.3057 -3 5 2 4 73.38 1.45 1.2903 -2 1 5 4 73.67 1.54 1.2859 0 5 4 4 73.97 2.70 1.2814 -1 7 2 4 74.03 1.17 1.2806 4 2 1 4 75.68 2.48 1.2567 -3 3 4 4 76.22 2.14 1.2491 1 7 2 4 78.22 1.53 1.2221 -2 5 4 4 79.11 1.80 1.2105 3 5 2 4 80.53 1.70 1.1928 -4 4 2 4 80.79 1.69 1.1895 4 2 2 4 81.60 1.34 1.1798 0 6 4 4 82.64 2.14 1.1676 -4 0 4 2 83.61 1.11 1.1564 0 8 2 4 84.34 1.03 1.1483 4 3 2 4 86.04 2.34 1.1300 -2 6 4 4 88.65 1.90 1.1033 -5 1 2 4 89.53 1.61 1.0947 -3 7 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.