Brownleeite Lebech B, Bernhard J, Freltoft T Journal of Physics: Condensed Matter 1 (1989) 6105-6122 Magnetic structures of cubic FeGe studied by small-angle neutron scattering _database_code_amcsd 0013254 CELL PARAMETERS: 4.5580 4.5580 4.5580 90.000 90.000 90.000 SPACE GROUP: P2_13 X-RAY WAVELENGTH: 1.541838 Cell Volume: 94.694 Density (g/cm3): 5.823 MAX. ABS. INTENSITY / VOLUME**2: 100.3246721 RIR: 5.610 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 27.68 17.77 3.2230 1 1 0 12 34.07 16.08 2.6316 1 1 1 4 39.54 6.16 2.2790 2 0 0 6 44.44 90.65 2.0384 2 1 0 12 44.44 9.35 2.0384 2 0 1 12 48.95 50.41 1.8608 2 1 1 12 60.98 3.46 1.5193 2 2 1 12 64.67 1.30 1.4414 3 1 0 12 68.24 9.91 1.3743 3 1 1 12 71.73 2.18 1.3158 2 2 2 4 75.15 4.15 1.2642 3 0 2 12 75.15 1.16 1.2642 3 2 0 12 78.52 21.38 1.2182 3 1 2 12 78.52 2.94 1.2182 3 2 1 12 85.15 6.74 1.1395 4 0 0 6 88.43 2.15 1.1055 4 1 0 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.