Tenorite Asbrink S, Waskowska A Journal of Physics: Condensed Matter 3 (1991) 8173-8180 CuO: x-ray single-crystal structure determination at 196 K and room temperature Note: T = 196 K Locality: synthetic _database_code_amcsd 0018823 CELL PARAMETERS: 4.6893 3.4268 5.1321 90.000 99.653 90.000 SPACE GROUP: Cc X-RAY WAVELENGTH: 1.541838 Cell Volume: 81.302 Density (g/cm3): 6.498 MAX. ABS. INTENSITY / VOLUME**2: 94.40003903 RIR: 4.731 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 32.52 6.10 2.7529 1 1 0 2 35.49 30.13 2.5297 0 0 2 1 35.53 80.45 2.5264 -1 1 1 2 38.77 100.00 2.3227 1 1 1 2 38.97 23.54 2.3115 2 0 0 1 46.25 1.66 1.9629 -1 1 2 2 48.70 29.02 1.8696 -2 0 2 1 51.44 1.10 1.7764 1 1 2 2 53.48 11.62 1.7134 0 2 0 2 58.42 15.37 1.5796 2 0 2 1 61.55 21.45 1.5067 -1 1 3 2 65.83 16.91 1.4186 0 2 2 2 66.24 16.45 1.4109 -3 1 1 2 68.03 10.34 1.3781 1 1 3 2 68.12 14.95 1.3765 2 2 0 2 72.50 8.38 1.3037 3 1 1 2 75.11 6.24 1.2649 0 0 4 1 75.22 7.39 1.2632 -2 2 2 2 80.16 2.51 1.1974 -2 0 4 1 82.32 5.64 1.1713 -3 1 3 2 83.18 5.41 1.1614 2 2 2 2 83.68 4.36 1.1557 4 0 0 1 86.52 2.05 1.1249 -4 0 2 1 89.77 7.23 1.0924 -1 3 1 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.