Cl5 D2 Fe K2 O Gabas M, Palacio F, Rodriguez-Carvajal J, Visser D Journal of Physics: Condensed Matter 7 (1995) 4725-4738 Magnetic structures of the three-dimensional Heisenberg antiferromagnets K2FeCl5*(D2O) and Rb2FeCl5*(D2O) _cod_database_code 1006101 _database_code_amcsd 0013274 CELL PARAMETERS: 13.4389 9.6025 6.9789 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 900.606 Density (g/cm3): 2.428 MAX. ABS. INTENSITY / VOLUME**2: 12.93016326 RIR: 1.734 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.70 57.43 5.6454 0 1 1 4 16.10 50.29 5.5054 2 1 0 4 17.04 3.66 5.2048 1 1 1 8 18.33 21.61 4.8405 2 0 1 4 18.48 4.24 4.8012 0 2 0 2 23.44 1.22 3.7946 1 2 1 8 25.53 1.64 3.4894 0 0 2 2 26.14 11.64 3.4088 2 2 1 8 26.39 8.33 3.3775 1 0 2 4 26.53 7.53 3.3597 4 0 0 2 29.51 17.81 3.0272 4 0 1 4 30.14 26.98 2.9651 3 2 1 8 30.33 6.01 2.9473 2 1 2 8 30.73 6.57 2.9094 0 3 1 4 30.95 10.50 2.8897 2 3 0 4 30.97 5.62 2.8871 4 1 1 8 31.70 17.02 2.8227 0 2 2 4 32.41 57.57 2.7624 1 2 2 8 32.53 43.82 2.7528 3 0 2 4 32.53 56.18 2.7527 4 2 0 4 34.46 1.83 2.6024 2 2 2 8 35.04 3.52 2.5607 4 2 1 8 35.80 1.07 2.5082 5 0 1 4 37.04 2.62 2.4268 5 1 1 8 37.15 32.07 2.4202 4 0 2 4 37.46 56.31 2.4006 0 4 0 2 38.35 1.06 2.3469 4 1 2 8 39.31 3.19 2.2922 1 0 3 4 40.53 2.12 2.2256 2 3 2 8 41.04 1.14 2.1994 4 3 1 8 41.06 7.97 2.1983 2 0 3 4 41.80 4.91 2.1612 4 2 2 8 42.01 4.19 2.1507 2 4 1 8 42.38 3.68 2.1327 6 0 1 4 42.45 16.70 2.1293 5 0 2 4 43.53 5.68 2.0788 5 1 2 8 43.76 2.31 2.0686 1 2 3 8 44.91 5.26 2.0184 3 1 3 8 46.41 2.78 1.9567 1 4 2 8 46.49 3.01 1.9532 4 4 0 4 46.60 4.12 1.9490 6 2 1 8 47.97 2.63 1.8966 3 2 3 8 48.28 1.98 1.8849 6 0 2 4 48.39 6.68 1.8810 4 4 1 8 48.53 3.34 1.8757 4 1 3 8 49.21 3.40 1.8517 0 5 1 4 49.22 3.49 1.8511 7 0 1 4 49.27 3.37 1.8496 6 1 2 8 49.35 2.13 1.8466 2 5 0 4 50.44 19.35 1.8093 3 4 2 8 51.55 2.76 1.7729 5 3 2 8 51.99 2.73 1.7590 5 0 3 4 52.76 2.16 1.7349 3 3 3 8 52.92 7.67 1.7302 1 0 4 4 53.78 17.04 1.7044 4 4 2 8 53.84 2.93 1.7028 1 1 4 8 54.32 2.91 1.6887 2 0 4 4 54.63 6.20 1.6799 8 0 0 2 55.42 2.27 1.6578 1 4 3 8 56.01 2.15 1.6418 4 3 3 8 56.09 1.38 1.6398 0 2 4 4 56.33 3.18 1.6332 8 0 1 4 56.61 1.83 1.6258 3 0 4 4 56.67 2.02 1.6242 6 3 2 8 56.77 1.44 1.6217 4 5 1 8 56.79 5.05 1.6212 2 4 3 8 57.21 3.31 1.6101 8 1 1 8 57.83 2.67 1.5944 6 4 1 8 57.88 1.86 1.5931 2 2 4 8 57.89 10.77 1.5930 5 4 2 8 59.81 3.95 1.5462 8 2 1 8 60.08 1.59 1.5399 3 2 4 8 60.86 1.66 1.5221 1 3 4 8 62.66 1.48 1.4825 6 4 2 8 63.09 1.99 1.4737 4 2 4 8 63.11 2.24 1.4732 3 6 1 8 63.46 2.69 1.4659 7 4 1 8 64.00 1.83 1.4548 8 3 1 8 64.00 1.16 1.4547 0 6 2 4 64.42 4.69 1.4463 1 6 2 8 64.49 4.32 1.4449 4 6 0 4 65.44 1.49 1.4261 5 5 2 8 65.82 2.23 1.4189 5 4 3 8 66.03 3.29 1.4150 7 2 3 8 66.49 1.62 1.4062 3 5 3 8 66.63 6.58 1.4036 1 4 4 8 67.46 1.15 1.3883 1 0 5 4 67.86 2.45 1.3812 2 4 4 8 68.13 5.44 1.3764 8 4 0 4 69.63 2.84 1.3503 8 4 1 8 69.88 1.73 1.3461 3 4 4 8 69.93 1.12 1.3452 6 5 2 8 71.27 2.75 1.3231 6 2 4 8 71.47 1.12 1.3199 9 2 2 8 73.32 1.80 1.2912 7 0 4 4 73.70 1.01 1.2855 1 5 4 8 75.68 2.08 1.2566 9 0 3 4 76.58 1.36 1.2442 8 5 1 8 76.98 1.92 1.2387 5 0 5 4 79.80 1.25 1.2018 1 4 5 8 79.92 3.66 1.2003 0 8 0 2 82.66 1.38 1.1673 11 2 1 8 84.82 1.12 1.1431 8 6 1 8 85.37 2.19 1.1371 7 4 4 8 86.36 1.37 1.1266 9 1 4 8 86.88 1.04 1.1212 7 1 5 8 87.65 2.65 1.1133 9 4 3 8 88.40 1.66 1.1058 12 0 1 4 88.91 2.55 1.1008 5 4 5 8 88.96 2.72 1.1003 3 8 2 8 89.08 1.03 1.0991 4 0 6 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.