Co Mn Sb Senateur J, Rouault A, Fruchart R Journal of Solid State Chemistry 5 (1972) 226-228 Structure and alloy chemistry of metastable Ge Sb _cod_database_code 1008962 _database_code_amcsd 0016827 CELL PARAMETERS: 11.7460 11.7460 11.7460 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1620.578 Density (g/cm3): 7.725 MAX. ABS. INTENSITY / VOLUME**2: 279.6943795 RIR: 11.789 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.05 1.33 6.7816 1 1 1 8 25.15 1.06 3.5416 3 1 1 24 26.28 19.92 3.3908 2 2 2 8 30.44 33.83 2.9365 4 0 0 6 33.25 2.69 2.6947 3 3 1 24 39.88 5.58 2.2605 5 1 1 24 43.59 100.00 2.0764 4 4 0 12 51.62 7.83 1.7708 6 2 2 24 54.09 7.55 1.6954 4 4 4 8 60.55 1.34 1.5292 5 5 3 24 63.34 13.47 1.4683 8 0 0 6 69.80 2.65 1.3474 6 6 2 24 71.89 8.28 1.3132 8 4 0 24 77.53 1.12 1.2313 9 3 1 48 80.04 23.07 1.1988 8 4 4 24 85.52 2.58 1.1355 9 5 1 48 86.01 1.27 1.1303 10 2 2 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.