Cu3 Mn4 O12 Th Deschizeaux M, Loubert J, Vegas A, Collomb A, Chenavas J, Marezio M Journal of Solid State Chemistry 19 (1976) 45-51 Synthetis and crystal structure of (Th Cu3) ((Mn2)^3+^ (Mn2)^4+^)O12, a new ferrimagnetic Perovskite-like compound _cod_database_code 1008192 _database_code_amcsd 0016129 CELL PARAMETERS: 7.3590 7.3590 7.3590 90.000 90.000 90.000 SPACE GROUP: Im3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 398.526 Density (g/cm3): 6.953 MAX. ABS. INTENSITY / VOLUME**2: 231.8395566 RIR: 10.858 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.04 36.34 5.2036 1 1 0 12 24.19 9.92 3.6795 2 0 0 6 29.74 13.20 3.0043 2 1 1 24 34.47 100.00 2.6018 2 2 0 12 38.69 12.32 2.3271 3 0 1 12 38.69 1.52 2.3271 3 1 0 12 42.56 8.90 2.1244 2 2 2 8 46.15 3.08 1.9668 3 2 1 24 46.15 12.32 1.9668 3 1 2 24 49.55 23.87 1.8398 4 0 0 6 52.78 3.58 1.7345 4 1 1 24 55.87 2.56 1.6455 4 0 2 12 55.87 1.14 1.6455 4 2 0 12 58.86 1.61 1.5689 3 3 2 24 61.76 39.94 1.5021 4 2 2 24 64.57 1.81 1.4432 4 3 1 24 64.57 1.98 1.4432 4 1 3 24 70.03 1.30 1.3436 5 2 1 24 72.68 10.30 1.3009 4 4 0 12 75.30 1.64 1.2621 5 3 0 12 77.89 1.67 1.2265 4 4 2 24 80.45 2.14 1.1938 5 2 3 24 82.99 5.65 1.1636 6 0 2 12 82.99 6.60 1.1636 6 2 0 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.