K0.85 Nb1.15 O5 Ti0.85 Rebbah A, Desgardin G, Raveau B Journal of Solid State Chemistry 31 (1980) 321-328 Nonstoichiometric oxides with a layer structure: The compounds A1-x(Ti1-xM1+x)O5 _cod_database_code 1001082 _database_code_amcsd 0013374 CELL PARAMETERS: 6.4740 3.8000 18.7650 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 461.642 Density (g/cm3): 3.751 MAX. ABS. INTENSITY / VOLUME**2: 42.18737753 RIR: 3.662 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.43 100.00 9.3825 0 0 2 2 14.47 6.98 6.1200 1 0 1 4 16.64 15.52 5.3286 1 0 2 4 18.92 2.54 4.6912 0 0 4 2 19.74 11.01 4.4984 1 0 3 4 23.89 17.08 3.7244 0 1 1 4 27.46 49.83 3.2477 0 1 3 4 27.56 35.47 3.2370 2 0 0 2 27.97 1.61 3.1899 2 0 1 4 29.18 2.97 3.0600 2 0 2 4 30.80 56.04 2.9029 1 1 3 8 31.11 4.56 2.8749 2 0 3 4 31.78 37.33 2.8161 1 0 6 4 33.56 1.77 2.6702 0 1 5 4 36.27 3.68 2.4768 1 0 7 4 36.40 1.60 2.4685 1 1 5 8 36.46 7.93 2.4642 2 1 0 4 36.66 2.12 2.4512 2 0 5 4 39.30 10.28 2.2927 2 1 3 8 40.92 13.62 2.2053 1 0 8 4 41.21 1.78 2.1905 0 1 7 4 42.15 1.05 2.1439 3 0 1 4 43.01 5.60 2.1031 3 0 2 4 44.41 10.16 2.0400 3 0 3 4 46.31 2.08 1.9605 3 0 4 4 47.68 2.46 1.9074 1 1 8 8 47.88 18.52 1.9000 0 2 0 2 48.51 1.92 1.8765 0 0 10 2 48.77 2.15 1.8672 3 1 1 8 48.91 2.70 1.8622 0 2 2 4 49.89 4.12 1.8279 0 1 9 4 50.80 6.63 1.7974 3 1 3 8 51.03 1.39 1.7896 1 2 2 8 51.45 5.22 1.7762 3 0 6 4 51.98 14.74 1.7591 1 1 9 8 52.18 1.97 1.7529 2 0 9 4 52.27 1.20 1.7503 1 2 3 8 52.52 1.43 1.7423 3 1 4 8 54.69 4.04 1.6784 3 1 5 8 56.13 7.49 1.6386 2 2 0 4 56.70 1.29 1.6234 2 0 10 4 57.25 6.93 1.6091 3 1 6 8 57.94 3.19 1.5917 2 1 9 8 58.08 1.79 1.5881 3 0 8 4 58.20 1.31 1.5851 2 2 3 8 58.61 10.69 1.5750 1 2 6 8 58.94 2.50 1.5669 4 0 3 4 59.08 1.50 1.5637 0 0 12 2 59.39 3.99 1.5563 0 1 11 4 60.51 2.20 1.5300 4 0 4 4 61.26 3.02 1.5132 1 1 11 8 62.36 3.86 1.4891 4 1 0 4 62.49 1.41 1.4862 4 0 5 4 63.49 2.65 1.4653 3 1 8 8 64.31 1.57 1.4486 4 1 3 8 64.76 5.56 1.4395 1 2 8 8 66.30 2.29 1.4098 3 2 2 8 66.39 1.18 1.4081 2 0 12 4 66.68 3.41 1.4026 2 1 11 8 67.11 2.64 1.3948 3 1 9 8 67.35 4.26 1.3904 3 2 3 8 71.45 3.13 1.3203 2 1 12 8 72.63 2.11 1.3017 4 1 7 8 72.90 2.95 1.2975 3 2 6 8 73.51 1.12 1.2883 2 2 9 8 76.77 1.76 1.2415 0 3 3 4 77.00 1.29 1.2384 2 0 14 4 78.44 2.48 1.2193 1 3 3 8 78.49 1.21 1.2185 3 2 8 8 79.25 1.74 1.2089 4 2 3 8 79.36 1.09 1.2074 0 2 12 4 80.62 1.55 1.1917 4 2 4 8 81.80 1.23 1.1774 2 1 14 8 82.38 1.02 1.1706 4 2 5 8 83.38 1.07 1.1591 2 3 3 8 85.00 2.19 1.1411 5 1 6 8 85.92 1.04 1.1313 2 2 12 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.