K3Mg4LiSi12O30 Nguyen N, Choisnet J, Raveau B Journal of Solid State Chemistry 34 (1980) 1-9 Silicates synthetiques a structure milarite Locality: synthetic _database_code_amcsd 0013393 CELL PARAMETERS: 10.2530 10.2530 14.0400 90.000 90.000 120.000 SPACE GROUP: P6/mcc X-RAY WAVELENGTH: 1.541838 Cell Volume: 1278.203 Density (g/cm3): 2.698 MAX. ABS. INTENSITY / VOLUME**2: 10.53487262 RIR: 1.272 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.61 4.09 7.0200 0 0 2 2 17.30 5.72 5.1265 1 1 0 6 20.00 56.96 4.4397 2 0 0 6 21.46 5.60 4.1401 1 1 2 12 23.71 46.25 3.7523 2 0 2 12 25.38 19.98 3.5100 0 0 4 2 27.32 17.65 3.2642 1 0 4 12 27.32 82.35 3.2641 2 1 1 24 30.20 7.07 2.9598 3 0 0 6 30.87 70.88 2.8962 1 1 4 12 32.52 27.02 2.7534 2 0 4 12 32.84 12.55 2.7273 2 1 3 24 32.84 2.26 2.7273 3 0 2 12 35.01 30.42 2.5633 2 2 0 6 36.48 6.28 2.4627 3 1 0 12 37.06 9.52 2.4257 3 1 1 24 38.47 2.26 2.3400 0 0 6 2 38.75 2.92 2.3238 3 1 2 24 39.84 2.65 2.2627 1 0 6 12 39.84 10.57 2.2627 3 0 4 12 41.43 10.71 2.1794 3 1 3 24 42.72 8.55 2.1165 4 0 2 12 43.73 3.15 2.0701 2 0 6 12 43.73 5.70 2.0700 2 2 4 12 44.47 2.71 2.0371 3 2 0 12 44.97 14.64 2.0160 3 1 4 24 46.41 4.05 1.9564 3 2 2 24 46.89 8.67 1.9376 4 1 0 12 47.36 8.00 1.9194 4 1 1 24 49.21 13.14 1.8515 3 1 5 24 51.01 1.00 1.7903 4 1 3 24 51.46 3.10 1.7759 5 0 0 6 52.11 10.35 1.7550 0 0 8 2 52.99 6.63 1.7282 2 2 6 12 53.20 1.97 1.7217 2 1 7 24 53.63 1.85 1.7088 3 3 0 6 54.06 6.10 1.6963 4 1 4 24 55.12 2.41 1.6662 4 2 1 24 56.37 3.04 1.6321 2 0 8 12 56.38 1.02 1.6321 4 2 2 24 58.22 9.80 1.5846 5 1 1 24 60.23 12.03 1.5364 3 3 4 12 61.22 1.07 1.5139 4 2 4 24 61.42 4.06 1.5096 3 0 8 12 61.42 2.21 1.5095 5 1 3 24 62.20 2.14 1.4924 4 1 6 24 62.79 2.09 1.4799 6 0 0 6 64.33 14.23 1.4481 2 2 8 12 64.33 2.36 1.4481 6 0 2 12 64.71 1.50 1.4404 4 2 5 24 65.67 13.35 1.4218 5 2 0 12 66.04 1.21 1.4146 2 1 9 24 66.05 2.54 1.4146 5 2 1 24 67.17 2.41 1.3936 4 1 7 24 67.55 3.48 1.3867 5 1 5 24 68.85 1.56 1.3637 4 2 6 24 68.85 3.56 1.3636 6 0 4 12 70.32 2.18 1.3387 2 0 10 12 70.87 1.70 1.3296 3 2 8 24 71.60 13.06 1.3178 3 1 9 24 71.60 1.62 1.3178 5 1 6 24 72.69 1.08 1.3008 4 1 8 24 73.06 1.30 1.2952 4 3 5 24 74.85 2.22 1.2685 7 0 0 6 75.21 4.50 1.2633 5 3 1 24 77.88 1.46 1.2266 6 2 1 24 78.05 4.51 1.2243 5 3 3 24 78.93 2.24 1.2128 6 2 2 24 79.64 4.71 1.2039 4 4 4 12 80.51 1.20 1.1930 2 1 11 24 80.51 1.29 1.1930 7 0 4 12 80.51 1.12 1.1930 5 3 4 24 81.04 2.32 1.1866 4 0 10 12 83.65 1.93 1.1560 5 3 5 24 85.04 1.65 1.1407 1 1 12 12 87.47 2.90 1.1152 5 1 9 24 87.47 3.40 1.1152 7 1 4 24 88.50 6.98 1.1048 5 2 8 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.