K3 Li Mg4 O30 Si12 Nguyen N, Choisnet J, Raveau B Journal of Solid State Chemistry 34 (1980) 1-9 Silicates synthetiques a structure milarite _cod_database_code 1001141 _database_code_amcsd 0013400 CELL PARAMETERS: 10.2530 10.2530 14.0400 90.000 90.000 120.000 SPACE GROUP: P6/mcc X-RAY WAVELENGTH: 1.541838 Cell Volume: 1278.203 Density (g/cm3): 2.698 MAX. ABS. INTENSITY / VOLUME**2: 10.58040307 RIR: 1.277 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.61 4.12 7.0200 0 0 2 2 17.30 5.92 5.1265 1 1 0 6 20.00 56.94 4.4397 2 0 0 6 21.46 5.88 4.1401 1 1 2 12 23.71 45.04 3.7523 2 0 2 12 25.38 20.31 3.5100 0 0 4 2 27.32 17.63 3.2642 1 0 4 12 27.32 82.37 3.2641 2 1 1 24 30.20 6.85 2.9598 3 0 0 6 30.87 69.93 2.8962 1 1 4 12 32.52 27.10 2.7534 2 0 4 12 32.84 12.70 2.7273 2 1 3 24 32.84 1.98 2.7273 3 0 2 12 35.01 30.29 2.5633 2 2 0 6 36.48 6.16 2.4627 3 1 0 12 37.06 10.27 2.4257 3 1 1 24 38.47 1.93 2.3400 0 0 6 2 38.75 2.40 2.3238 3 1 2 24 39.84 2.34 2.2627 1 0 6 12 39.84 9.90 2.2627 3 0 4 12 41.43 9.56 2.1794 3 1 3 24 42.72 7.89 2.1165 4 0 2 12 43.73 2.64 2.0701 2 0 6 12 43.73 4.93 2.0700 2 2 4 12 44.47 2.83 2.0371 3 2 0 12 44.97 14.71 2.0160 3 1 4 24 46.41 3.44 1.9564 3 2 2 24 46.89 7.83 1.9376 4 1 0 12 47.36 7.76 1.9194 4 1 1 24 49.21 14.08 1.8515 3 1 5 24 51.46 3.16 1.7759 5 0 0 6 52.11 10.27 1.7550 0 0 8 2 52.99 7.16 1.7282 2 2 6 12 53.20 1.96 1.7217 2 1 7 24 53.63 2.04 1.7088 3 3 0 6 54.06 5.84 1.6963 4 1 4 24 55.12 2.49 1.6662 4 2 1 24 56.37 3.13 1.6321 2 0 8 12 58.22 10.22 1.5846 5 1 1 24 60.23 11.78 1.5364 3 3 4 12 61.42 3.70 1.5096 3 0 8 12 61.42 2.39 1.5095 5 1 3 24 62.20 1.72 1.4924 4 1 6 24 62.79 1.86 1.4799 6 0 0 6 64.33 13.82 1.4481 2 2 8 12 64.33 2.56 1.4481 6 0 2 12 64.71 1.62 1.4404 4 2 5 24 65.67 13.31 1.4218 5 2 0 12 66.04 1.44 1.4146 2 1 9 24 66.05 2.45 1.4146 5 2 1 24 67.17 2.20 1.3936 4 1 7 24 67.55 3.98 1.3867 5 1 5 24 68.85 1.24 1.3637 4 2 6 24 68.85 3.33 1.3636 6 0 4 12 70.32 2.04 1.3387 2 0 10 12 70.87 1.78 1.3296 3 2 8 24 71.60 13.62 1.3178 3 1 9 24 71.60 1.30 1.3178 5 1 6 24 73.06 1.36 1.2952 4 3 5 24 74.85 2.30 1.2685 7 0 0 6 75.21 4.66 1.2633 5 3 1 24 77.88 1.56 1.2266 6 2 1 24 78.05 4.43 1.2243 5 3 3 24 78.93 1.76 1.2128 6 2 2 24 79.64 4.52 1.2039 4 4 4 12 80.51 1.10 1.1930 2 1 11 24 80.51 1.35 1.1930 7 0 4 12 80.51 1.15 1.1930 5 3 4 24 81.04 2.00 1.1866 4 0 10 12 83.65 2.22 1.1560 5 3 5 24 85.04 1.51 1.1407 1 1 12 12 86.26 1.05 1.1277 6 2 5 24 87.47 3.35 1.1152 5 1 9 24 87.47 3.24 1.1152 7 1 4 24 88.50 6.90 1.1048 5 2 8 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.