Beta - fergusonite-(Ce) Santoro A, Marezio M, Roth R S, Minor D Journal of Solid State Chemistry 35 (1980) 167-175 Neutron powder diffraction study of the structures of CeTaO4, CeNbO4, and NdTaO4 Locality: synthetic _database_code_amcsd 0013406 CELL PARAMETERS: 5.5350 11.3991 5.1590 90.000 94.600 90.000 SPACE GROUP: I2/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 324.454 Density (g/cm3): 6.080 MAX. ABS. INTENSITY / VOLUME**2: 134.0486796 RIR: 7.179 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.55 1.62 5.6996 0 2 0 2 18.93 6.32 4.6875 0 1 1 4 27.61 100.00 3.2309 -1 2 1 4 28.52 5.59 3.1294 1 3 0 4 29.23 83.66 3.0556 1 2 1 4 31.39 21.36 2.8498 0 4 0 2 32.46 21.60 2.7586 2 0 0 2 34.89 14.68 2.5712 0 0 2 2 38.24 1.33 2.3537 -1 1 2 4 39.08 3.83 2.3049 2 1 1 4 40.28 4.06 2.2391 1 4 1 4 43.42 6.32 2.0842 0 5 1 4 44.58 2.15 2.0325 -1 3 2 4 45.78 26.17 1.9821 2 4 0 4 46.30 15.48 1.9609 -2 0 2 2 46.73 4.04 1.9437 1 3 2 4 47.64 24.17 1.9090 0 4 2 4 50.42 11.59 1.8099 2 0 2 2 53.60 11.01 1.7098 -1 6 1 4 54.04 15.63 1.6968 -3 2 1 4 54.30 2.40 1.6895 -2 5 1 4 54.55 9.87 1.6822 1 6 1 4 55.51 1.78 1.6554 3 3 0 4 56.17 2.10 1.6375 2 5 1 4 56.85 10.26 1.6196 3 2 1 4 57.01 8.92 1.6154 -2 4 2 4 57.32 10.88 1.6074 -1 2 3 4 59.15 4.31 1.5618 1 7 0 4 60.02 10.17 1.5413 1 2 3 4 60.61 7.34 1.5278 2 4 2 4 65.51 1.81 1.4249 0 8 0 2 67.96 3.56 1.3793 4 0 0 2 69.73 1.82 1.3485 -1 7 2 4 71.37 1.50 1.3216 1 7 2 4 72.88 3.17 1.2980 -3 6 1 4 73.69 3.49 1.2856 0 0 4 2 74.46 4.84 1.2742 -3 2 3 4 75.03 3.17 1.2660 2 8 0 4 75.28 4.96 1.2624 3 6 1 4 75.47 1.25 1.2597 -2 5 3 4 75.57 2.58 1.2582 -4 0 2 2 75.68 4.01 1.2566 -1 6 3 4 76.42 3.33 1.2463 0 8 2 4 76.77 3.97 1.2415 4 4 0 4 77.64 2.13 1.2298 0 9 1 4 78.06 3.36 1.2243 1 6 3 4 78.44 1.09 1.2192 3 7 0 4 79.72 1.87 1.2028 -2 0 4 2 80.20 1.11 1.1969 2 5 3 4 81.55 4.41 1.1804 3 2 3 4 81.86 2.00 1.1768 4 0 2 2 82.27 3.04 1.1719 0 4 4 4 83.95 2.02 1.1527 -2 8 2 4 84.10 3.38 1.1510 -4 4 2 4 85.91 2.34 1.1313 -2 9 1 4 85.94 1.62 1.1311 2 0 4 2 86.51 1.49 1.1250 -3 7 2 4 87.04 1.93 1.1196 2 8 2 4 87.45 1.41 1.1153 2 9 1 4 88.17 3.22 1.1081 -2 4 4 4 89.54 1.17 1.0946 -1 10 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.