Cu La0.74 O4 Sr1.2 Nguyen N, Choisnet J, Hervieu M, Raveau B Journal of Solid State Chemistry 39 (1981) 120-127 Oxygen Defect K2NiF4-Type Oxides: The Compounds La2-xSrxCuO4-x/2+d _cod_database_code 1001204 _database_code_amcsd 0013418 CELL PARAMETERS: 18.8040 18.8040 12.9410 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 4575.814 Density (g/cm3): 6.076 MAX. ABS. INTENSITY / VOLUME**2: 121.2727221 RIR: 6.499 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 6.65 1.28 13.2964 1 1 0 4 13.69 7.67 6.4705 0 0 2 2 14.90 2.03 5.9463 3 1 0 8 20.03 1.45 4.4321 3 3 0 4 24.65 5.88 3.6114 5 0 1 8 27.57 6.86 3.2352 0 0 4 2 31.56 99.76 2.8347 5 0 3 8 33.70 62.30 2.6593 5 5 0 4 34.32 1.28 2.6131 3 3 4 8 35.44 1.07 2.5330 7 2 1 16 40.72 1.75 2.2160 7 2 3 16 41.63 1.91 2.1697 8 3 1 16 41.89 16.03 2.1568 0 0 6 2 42.39 14.64 2.1321 5 0 5 8 44.08 16.47 2.0544 5 5 4 8 46.31 2.19 1.9604 8 3 3 16 48.41 26.62 1.8804 10 0 0 4 54.80 13.88 1.6751 5 5 6 8 55.38 4.57 1.6591 5 0 7 8 56.61 2.17 1.6257 10 0 4 8 56.92 3.63 1.6176 0 0 8 2 58.94 25.90 1.5670 10 5 3 16 65.90 10.18 1.4174 10 0 6 8 66.27 5.60 1.4103 10 5 5 16 67.81 4.10 1.3820 5 5 8 8 70.06 1.31 1.3431 5 0 9 8 70.87 5.43 1.3296 10 10 0 4 76.58 1.98 1.2441 10 5 7 16 77.90 3.99 1.2263 10 0 8 8 79.64 3.62 1.2038 15 0 3 8 80.82 4.71 1.1893 15 5 0 8 82.98 1.55 1.1636 5 5 10 8 85.86 3.35 1.1318 10 10 6 8 86.72 5.04 1.1228 5 0 11 8 87.36 1.31 1.1162 15 5 4 16 89.72 1.28 1.0929 10 5 9 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.