D1.8H0.2TaWO6 Groult D, Pannetier, Raveau B Journal of Solid State Chemistry 41 (1982) 277-285 Neutron diffraction study of the defect pyrochlores TaWO5.5, HTaWO6, H2Ta2O6, and HTaWO6*H2 O _cod_database_code 1001215 _database_code_amcsd 0013470 CELL PARAMETERS: 10.4421 10.4421 10.4421 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1138.580 Density (g/cm3): 5.385 MAX. ABS. INTENSITY / VOLUME**2: 317.9171233 RIR: 19.224 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.69 100.00 6.0287 1 1 1 8 28.35 47.05 3.1484 3 1 1 24 29.64 53.60 3.0144 2 2 2 8 34.35 17.91 2.6105 4 0 0 6 37.54 13.84 2.3956 3 3 1 24 45.12 7.79 2.0096 5 1 1 24 45.12 7.14 2.0096 3 3 3 8 49.37 21.07 1.8459 4 4 0 12 51.80 16.85 1.7650 5 3 1 48 57.91 6.51 1.5924 5 3 3 24 58.64 20.58 1.5742 6 2 2 24 61.53 5.91 1.5072 4 4 4 8 63.64 5.75 1.4622 5 5 1 24 63.64 4.26 1.4622 7 1 1 24 69.09 6.83 1.3594 7 3 1 48 69.09 2.47 1.3594 5 5 3 24 72.40 2.84 1.3053 8 0 0 6 74.36 1.46 1.2757 7 3 3 24 79.49 3.06 1.2057 7 5 1 48 80.12 7.18 1.1978 6 6 2 24 82.65 6.55 1.1675 8 4 0 24 84.54 2.88 1.1462 7 5 3 48 84.54 1.61 1.1462 9 1 1 24 89.54 3.09 1.0946 9 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.