Al Cr2 Li2 O8 Sb Tarte P, Cahay R, Preudhomme J, Hervieu M, Choisnet J, Raveau B Journal of Solid State Chemistry 44 (1982) 282-289 Hexagonal-spinel transitions in antimonates Li2Cr(3-x)M(III)xSbO8 _cod_database_code 1001227 _database_code_amcsd 0013487 CELL PARAMETERS: 5.7960 5.7960 9.4660 90.000 90.000 120.000 SPACE GROUP: P6_3mc X-RAY WAVELENGTH: 1.541838 Cell Volume: 275.394 Density (g/cm3): 4.758 MAX. ABS. INTENSITY / VOLUME**2: 68.16996681 RIR: 4.665 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.67 8.90 5.0195 1 0 0 6 18.75 3.71 4.7330 0 0 2 1 20.02 100.00 4.4346 1 0 1 6 25.87 30.41 3.4436 1 0 2 6 30.85 10.67 2.8980 1 1 0 6 33.55 33.91 2.6714 1 0 3 6 35.78 8.28 2.5097 2 0 0 6 36.35 46.47 2.4715 1 1 2 6 37.06 21.02 2.4259 2 0 1 6 38.02 4.41 2.3665 0 0 4 1 40.69 13.95 2.2173 2 0 2 6 46.22 22.39 1.9642 2 0 3 6 48.97 11.28 1.8602 2 1 1 12 49.74 7.31 1.8330 1 1 4 6 51.60 3.92 1.7714 1 0 5 6 51.92 10.70 1.7610 2 1 2 12 53.20 9.33 1.7218 2 0 4 6 54.87 1.70 1.6732 3 0 0 6 56.61 15.77 1.6259 2 1 3 12 58.51 10.35 1.5775 3 0 2 6 61.34 20.39 1.5114 2 0 5 6 61.62 1.32 1.5051 1 0 6 6 64.29 17.63 1.4490 2 2 0 6 67.61 5.25 1.3856 1 1 6 6 68.07 4.99 1.3773 3 1 1 12 68.71 2.40 1.3662 3 0 4 6 70.24 3.58 1.3401 2 1 5 12 70.51 2.46 1.3356 3 1 2 12 72.37 4.14 1.3057 1 0 7 6 74.50 5.17 1.2737 3 1 3 12 76.59 2.30 1.2440 4 0 1 6 77.20 3.75 1.2358 2 2 4 6 78.92 1.46 1.2130 2 1 6 12 81.31 1.47 1.1832 0 0 8 1 82.77 2.59 1.1660 4 0 3 6 84.38 2.53 1.1479 3 0 6 6 84.81 1.07 1.1431 3 2 1 12 86.84 1.46 1.1216 3 1 5 12 88.11 1.48 1.1086 4 0 4 6 88.87 3.11 1.1012 2 1 7 12 89.46 1.19 1.0955 1 1 8 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.