Al2 Cr Li2 O8 Sb Tarte P, Cahay R, Preudhomme J, Hervieu M, Choisnet J, Raveau B Journal of Solid State Chemistry 44 (1982) 282-289 Hexagonal-spinel transitions in antimonates Li2Cr(3-x)M(III)xSbO8 _cod_database_code 1001228 _database_code_amcsd 0013488 CELL PARAMETERS: 5.7030 5.7030 9.3920 90.000 90.000 120.000 SPACE GROUP: P6_3mc X-RAY WAVELENGTH: 1.541838 Cell Volume: 264.543 Density (g/cm3): 4.639 MAX. ABS. INTENSITY / VOLUME**2: 68.66664911 RIR: 4.819 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.96 9.41 4.9389 1 0 0 6 18.90 1.58 4.6960 0 0 2 1 20.32 100.00 4.3714 1 0 1 6 26.19 33.28 3.4032 1 0 2 6 31.37 12.89 2.8515 1 1 0 6 33.90 33.03 2.6442 1 0 3 6 36.38 6.03 2.4695 2 0 0 6 36.88 40.77 2.4373 1 1 2 6 37.66 14.59 2.3883 2 0 1 6 38.33 3.39 2.3480 0 0 4 1 41.31 12.69 2.1857 2 0 2 6 46.86 22.02 1.9389 2 0 3 6 48.78 1.07 1.8667 2 1 0 12 49.80 12.81 1.8309 2 1 1 12 50.34 7.51 1.8126 1 1 4 6 52.09 4.52 1.7557 1 0 5 6 52.77 7.80 1.7347 2 1 2 12 53.88 9.55 1.7016 2 0 4 6 55.84 2.14 1.6463 3 0 0 6 57.48 15.06 1.6033 2 1 3 12 59.50 9.00 1.5536 3 0 2 6 62.08 15.82 1.4950 2 0 5 6 62.21 1.43 1.4922 1 0 6 6 65.46 15.94 1.4258 2 2 0 6 68.36 6.14 1.3722 1 1 6 6 69.33 4.99 1.3555 3 1 1 12 69.77 2.41 1.3480 3 0 4 6 71.21 3.71 1.3241 2 1 5 12 71.78 2.67 1.3150 3 1 2 12 73.08 3.36 1.2948 1 0 7 6 75.80 4.89 1.2549 3 1 3 12 78.06 1.79 1.2242 4 0 1 6 78.48 3.11 1.2187 2 2 4 6 79.99 1.18 1.1994 2 1 6 12 82.09 1.36 1.1740 0 0 8 1 84.31 2.61 1.1486 4 0 3 6 85.62 2.93 1.1344 3 0 6 6 88.30 1.66 1.1068 3 1 5 12 89.73 1.61 1.0928 4 0 4 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.