Fe3 Li2 O8 Sb Tarte P, Cahay R, Preudhomme J, Hervieu M, Choisnet J, Raveau B Journal of Solid State Chemistry 44 (1982) 282-289 Hexagonal-spinel transitions in antimonates Li2Cr(3-x)M(III)xSbO8 _cod_database_code 1001232 _database_code_amcsd 0013492 CELL PARAMETERS: 8.4250 8.4250 8.4250 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 598.012 Density (g/cm3): 4.789 MAX. ABS. INTENSITY / VOLUME**2: 66.11187391 RIR: 4.495 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.24 10.09 4.8642 1 1 1 8 30.00 28.83 2.9787 2 2 0 12 35.33 100.00 2.5402 3 1 1 24 36.96 5.73 2.4321 2 2 2 8 42.94 23.53 2.1063 4 0 0 6 53.27 9.47 1.7197 4 2 2 24 56.78 26.98 1.6214 5 1 1 24 56.78 5.76 1.6214 3 3 3 8 62.35 44.20 1.4893 4 4 0 12 65.55 1.18 1.4241 5 3 1 48 70.72 3.37 1.3321 6 2 0 24 73.74 8.71 1.2848 5 3 3 24 74.74 3.48 1.2701 6 2 2 24 78.69 2.90 1.2160 4 4 4 8 86.43 3.83 1.1258 6 4 2 48 89.31 5.67 1.0968 5 5 3 24 89.31 7.98 1.0968 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.