Li2 O3 Sn Hodeau J, Marezio M, Santoro A, Roth R Journal of Solid State Chemistry 45 (1982) 170-179 Neutron Profile Refinement of the Structures of Li2SnO3 and Li2ZrO3 _cod_database_code 1008199 _database_code_amcsd 0016135 CELL PARAMETERS: 5.2889 9.1872 10.0260 90.000 100.348 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 479.241 Density (g/cm3): 4.967 MAX. ABS. INTENSITY / VOLUME**2: 92.41620564 RIR: 6.058 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.99 100.00 4.9315 0 0 2 2 19.32 4.91 4.5936 0 2 0 2 19.61 31.00 4.5273 1 1 0 4 20.26 10.19 4.3824 -1 1 1 4 21.34 24.77 4.1641 0 2 1 4 22.86 7.19 3.8904 1 1 1 4 24.53 17.40 3.6296 -1 1 2 4 26.52 4.61 3.3613 0 2 2 4 28.78 11.20 3.1022 1 1 2 4 31.02 2.82 2.8831 -1 1 3 4 33.52 6.32 2.6735 0 2 3 4 34.37 33.48 2.6095 -1 3 1 4 34.48 16.47 2.6014 2 0 0 2 36.02 14.56 2.4934 1 3 1 4 36.02 7.25 2.4931 -2 0 2 2 36.19 1.75 2.4821 1 1 3 4 36.44 7.14 2.4657 0 0 4 2 38.76 4.12 2.3233 -1 1 4 4 39.43 3.57 2.2855 -2 2 1 4 39.82 1.12 2.2636 2 2 0 4 40.32 3.53 2.2369 0 4 1 4 41.90 44.75 2.1562 -1 3 3 4 42.08 22.10 2.1472 2 0 2 2 42.34 3.16 2.1347 2 2 1 4 43.46 1.14 2.0821 0 4 2 4 44.50 2.77 2.0359 1 1 4 4 44.93 2.83 2.0175 -2 2 3 4 45.94 6.23 1.9755 -2 0 4 2 46.02 12.31 1.9722 1 3 3 4 48.34 2.69 1.8828 0 4 3 4 50.34 1.84 1.8125 0 2 5 4 52.55 2.10 1.7416 2 2 3 4 52.84 1.44 1.7326 1 5 0 4 52.88 1.98 1.7313 -2 4 1 4 53.72 1.29 1.7064 -3 1 2 4 53.79 1.93 1.7042 3 1 0 4 55.12 1.78 1.6661 -1 5 2 4 55.24 1.17 1.6630 2 4 1 4 55.56 8.97 1.6539 -1 3 5 4 55.79 4.45 1.6479 2 0 4 2 55.94 2.91 1.6438 0 0 6 2 56.49 1.32 1.6290 -1 1 6 4 56.92 1.64 1.6177 -2 2 5 4 57.38 1.61 1.6057 -2 4 3 4 60.32 1.01 1.5343 -3 1 4 4 60.46 6.02 1.5312 0 6 0 2 60.53 1.19 1.5295 3 1 2 4 60.61 12.00 1.5279 -3 3 1 4 61.03 5.83 1.5182 -2 0 6 2 61.17 11.54 1.5152 1 3 5 4 62.02 1.23 1.4964 0 4 5 4 63.63 5.08 1.4623 0 6 2 4 63.71 5.05 1.4608 -3 3 3 4 63.84 5.06 1.4581 3 3 1 4 71.49 3.11 1.3196 2 6 0 4 71.63 1.56 1.3174 -4 0 2 2 72.43 2.02 1.3048 -2 6 2 4 72.69 2.02 1.3008 0 6 4 4 72.70 2.00 1.3007 -3 3 5 4 72.95 1.98 1.2968 3 3 3 4 73.21 2.00 1.2928 -1 3 7 4 76.39 5.04 1.2467 2 6 2 4 76.40 2.53 1.2466 -4 0 4 2 77.41 2.40 1.2329 0 0 8 2 79.14 2.05 1.2102 -2 6 4 4 79.51 1.00 1.2054 4 0 2 2 79.89 1.36 1.2007 -2 0 8 2 80.07 2.71 1.1984 1 3 7 4 86.83 1.98 1.1217 2 6 4 4 86.90 1.44 1.1210 -3 3 7 4 86.95 1.43 1.1204 0 6 6 4 87.26 1.41 1.1173 3 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.